Ultradur® B 4406
聚丁烯對苯二甲酸酯(PBT)
德國巴斯夫-BASF Corporation
產(chǎn)品說明:
Ultradur B 4406 is an injection molding PBT grade grade with migration-free flame retardant offering a UL V0 rating.
Applications
Typical applications include relay housings, plug-in connectors, and switch and lamp parts.
ul證書號：E41871-233793
含添加劑：阻燃劑
材料特性：無遷移阻燃
材料用途：開關(guān)，連接器，外殼
加工方法：粒子注射成型
供貨地區(qū)：北美洲，亞太地區(qū)，歐洲
中國代理：蘇州希普能工程塑料
Ultradur® B 4406巴斯夫中文加工參數(shù)表
| 物理性能 | 額定值 | 單位制 | 測試方法 |
| 密度/比重 | 1.45 | g/cm³ | ASTM D792,ISO 1183 |
| 熔融體積流量（MVR）(250℃/2.16kg) | 30 | cm³/10min | ISO 1133 |
| 收縮率-流動(3.18 mm) | 1.5 | % | |
| 吸水率 | |||
| 飽和 | 0.40 | % | ASTM D570 |
| 飽和,23℃ | 0.40 | % | ISO 62 |
| 平衡,50% RH | 0.25 | % | ASTM D570 |
| 平衡,23℃,50% RH | 0.25 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 122.0 | ml/g | ISO 1628 |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
| 拉伸模量(23℃) | 3000 | MPa | ISO 527-1 |
| 抗張強度(屈服,23℃) | 65.0 | MPa | ASTM D638,ISO 527-2 |
| 伸長率(屈服,23℃) | 3.9 | % | ASTM D638,ISO 527-2 |
| 標稱拉伸斷裂應(yīng)變 | ISO 527-2 | ||
| -40℃ | 3.3 | % | |
| 23℃ | 3.5 | % | |
| 拉伸蠕變模量(1hr) | 1800 | MPa | ISO 899-1 |
| 沖擊性能 | 額定值 | 單位制 | 測試方法 |
| 簡支梁缺口沖擊強度 | ISO 179 | ||
| -30℃ | 4.0 | kJ/m² | |
| 23℃ | 4.0 | kJ/m² | |
| 簡支梁無缺口沖擊強度(23℃) | 50 | kJ/m² | ISO 179 |
| 懸壁梁缺口沖擊強度 | ASTM D256 | ||
| -40℃ | 37 | J/m | |
| 23℃ | 37 | J/m | |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
| 載荷下熱變形溫度 | |||
| 0.45 MPa,未退火 | 165 | ℃ | ASTM D648 |
| 0.45 MPa,未退火 | 170 | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 80.0 | ℃ | ASTM D648 |
| 1.8 MPa,未退火 | 60.0 | ℃ | ISO 75-2/A |
| 熔融峰值溫度 | 223 | ℃ | ASTM D3418,ISO 3146 |
| 線形熱膨脹系數(shù)-流動 | |||
| -- | 9.0E-5 | cm/cm/℃ | ASTM E831 |
| -- | 5.5E-5 | cm/cm/℃ | |
| RTI Elec | UL 746B | ||
| 0.75 mm | 125 | ℃ | |
| 1.5 mm | 125 | ℃ | |
| 3.0 mm | 125 | ℃ | |
| RTI Imp | UL 746B | ||
| 0.75 mm | 130 | ℃ | |
| 1.5 mm | 130 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| RTI | UL 746B | ||
| 0.75 mm | 140 | ℃ | |
| 1.5 mm | 140 | ℃ | |
| 3.0 mm | 140 | ℃ | |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
| 表面電阻率 | |||
| 1.50 mm | 1.0E+13 | ohms | ASTM D257 |
| -- | 1.0E+13 | ohms | IEC 60093 |
| 體積電阻率 | |||
| 1.50 mm | > 1.0E+15 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| 介電常數(shù) | IEC 60250 | ||
| 100 Hz | 3.30 | ||
| 1 MHz | 3.30 | ||
| 耗散因數(shù) | IEC 60250 | ||
| 100 Hz | 0.011 | ||
| 1 MHz | 0.017 | ||
| 漏電起痕指數(shù) | 250 | V | IEC 60112 |
| 可燃性 | 額定值 | 單位制 | 測試方法 |
| UL 阻燃等級 | UL 94 | ||
| 0.40 mm | V-0 | ||
| 0.75 mm | V-0 | ||
| 1.5 mm | V-0 | ||
| 3.0 mm | V-0 | ||
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 100到120 | ℃ | |
| 干燥時間 | 4.0 | hr | |
| 建議的最大水分含量 | 0.040 | % | |
| 加工（熔體）溫度 | 250到270 | ℃ | |
| 模具溫度 | 40到80 | ℃ | |
| 注塑壓力 | 3.50到12.5 | MPa | |
| 注射速度 | 快速 | ||
| 背壓 | < 1.00 | MPa | |