VALOX 357X
聚碳酸酯+PBT
SABIC
產(chǎn)品說(shuō)明:
VALOX 357X is an unreinforced, impact modified flame retardant Polybutylene Terephthalate/Polycarbonate (PBT/PC) injection moldable grade. It has excellent chemical resistance and a UL94V0@0.75mm and 5VA@2.5mm flame rating. This is a good candidate for applications in the electrical industry including bobbins, switches, and enclosures.
黃卡號(hào)碼：E45329-100963601、E45329-101284020
材料用途：Material Handling、Water Management、電氣/電子應(yīng)用領(lǐng)域、電氣元件、電器用具、電子顯示器、汽車(chē)的發(fā)動(dòng)機(jī)罩下的零件、醫(yī)療/護(hù)理用品、照明應(yīng)用
加工方法：注射成型
供貨地區(qū)：歐洲
| 物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 密度/比重 | 1.34 | g/cm³ | ASTM D792,ISO 1183 |
| 熔流率（熔體流動(dòng)速率） | ASTM D1238 | ||
| 250℃/5.0 kg | 9.6 | g/10 min | |
| 265℃/5.0 kg | 13 | g/10 min | |
| 266℃/5.0 kg | 13 | g/10 min | |
| 熔融體積流量（MVR） | ISO 1133 | ||
| 250℃/5.0 kg | 8.0 | cm³/10min | |
| 265℃/5.0 kg | 10 | cm³/10min | |
| 收縮率 | 內(nèi)部方法 | ||
| 垂直1 | 0.90 到 1.8 | % | |
| 流動(dòng)1 | 1.1 到 1.8 | % | |
| 流動(dòng):3.20 mm | 1.0 到 1.4 | % | |
| 吸水率 | ISO 62 | ||
| 飽和,23℃ | 0.50 | % | |
| 平衡,23℃,50% RH | 0.15 | % | |
| 室外適用性 | f1 | UL 746C | |
| 硬度 | 額定值 | 單位制 | 測(cè)試方法 |
| 洛氏硬度(R 計(jì)秤) | 115 | ISO 2039-2 | |
| 球壓硬度(H 358/30) | 115 | MPa | ISO 2039-1 |
| 機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 拉伸模量 | |||
| --2 | 2000 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-1/1 |
| 抗張強(qiáng)度 | |||
| 屈服3 | 50.0 | MPa | ASTM D638 |
| 屈服 | 50.0 | MPa | ISO 527-2/50 |
| 斷裂3 | 40.0 | MPa | ASTM D638 |
| 斷裂 | 40.0 | MPa | ISO 527-2/50 |
| 伸長(zhǎng)率 | |||
| 屈服3 | 5.0 | % | ASTM D638 |
| 屈服 | 5.0 | % | ISO 527-2/50 |
| 斷裂3 | 30 | % | ASTM D638 |
| 斷裂 | 30 | % | ISO 527-2/50 |
| 彎曲模量 | |||
| 50.0 mm 跨距4 | 2100 | MPa | ASTM D790 |
| --5 | 2000 | MPa | ISO 178 |
| 彎曲應(yīng)力 | |||
| --5,6 | 80.0 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距4 | 78.0 | MPa | ASTM D790 |
| 泰伯耐磨性(1000 Cycles,1000 g,CS-17 轉(zhuǎn)輪) | 33.0 | mg | 內(nèi)部方法 |
| 沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 簡(jiǎn)支梁缺口沖擊強(qiáng)度 | |||
| -30℃7 | 20 | kJ/m² | ISO 179/1eA,ISO 179/2C |
| 23℃7 | 45 | kJ/m² | ISO 179/1eA |
| 23℃ | 40 | kJ/m² | ISO 179/2C |
| 簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度7 | ISO 179/1eU,ISO 179/2U | ||
| -30℃ | 無(wú)斷裂 | ||
| 23℃ | 無(wú)斷裂 | ||
| 懸壁梁缺口沖擊強(qiáng)度 | |||
| -30℃ | 150 | J/m | ASTM D256 |
| 0℃ | 190 | J/m | ASTM D256 |
| 23℃ | 500 | J/m | ASTM D256 |
| -30℃8 | 15 | kJ/m² | ISO 180/1A |
| 0℃8 | 20 | kJ/m² | ISO 180/1A |
| 23℃8 | 40 | kJ/m² | ISO 180/1A |
| 無(wú)缺口懸臂梁沖擊 | ASTM D4812,ISO 180/1U | ||
| -30℃ | 無(wú)斷裂 | ||
| 23℃ | 無(wú)斷裂 | ||
| 裝有測(cè)量?jī)x表的落鏢沖擊(23℃,Total Energy) | 35.0 | J | ASTM D3763 |
| 熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 載荷下熱變形溫度 | |||
| 0.45 MPa,未退火,3.20 mm | 130 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,4.00 mm,100 mm 跨距9 | 135 | ℃ | ISO 75-2/Be |
| 0.45 MPa,未退火,4.00 mm,64.0 mm 跨距8 | 130 | ℃ | ISO 75-2/Bf |
| 1.8 MPa,未退火,3.20 mm | 85.0 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,100 mm 跨距9 | 85.0 | ℃ | ISO 75-2/Ae |
| 1.8 MPa,未退火,4.00 mm,64.0 mm 跨距8 | 85.0 | ℃ | ISO 75-2/Af |
| 維卡軟化溫度 | |||
| -- | 180 | ℃ | ASTM D152510,ISO 306/A5010 |
| -- | 145 | ℃ | ASTM D152511,ISO 306/B5011 |
| -- | 150 | ℃ | ISO 306/B120 |
| Ball Pressure Test(123 到 127℃) | 通過(guò) | IEC 60695-10-2 | |
| 線(xiàn)形熱膨脹系數(shù) | |||
| 流動(dòng):-40 到 40℃ | 9.2E-5 | cm/cm/℃ | ASTM E831 |
| 流動(dòng):23 到 80℃ | 1.0E-4 | cm/cm/℃ | ISO 11359-2 |
| 垂直:-40 到 40℃ | 8.4E-5 | cm/cm/℃ | ASTM E831 |
| 垂直:23 到 80℃ | 1.0E-4 | cm/cm/℃ | ISO 11359-2 |
| 導(dǎo)熱系數(shù) | 0.17 | W/m/K | ISO 8302 |
| RTI Elec | 120 | ℃ | UL 746B |
| RTI Imp | 120 | ℃ | UL 746B |
| RTI | 140 | ℃ | UL 746B |
| 電氣性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 表面電阻率 | > 1.0E+15 | ohms | IEC 60093 |
| 體積電阻率 | > 1.0E+15 | ohms·cm | ASTM D257,IEC 60093 |
| 介電強(qiáng)度 | |||
| 1.60 mm,in Oil | 25 | kV/mm | ASTM D149 |
| 3.20 mm,in Oil | 17 | kV/mm | ASTM D149 |
| 0.800 mm,在油中 | 34 | kV/mm | IEC 60243-1 |
| 1.60 mm,在油中 | 25 | kV/mm | IEC 60243-1 |
| 3.20 mm,在油中 | 17 | kV/mm | IEC 60243-1 |
| 介電常數(shù) | |||
| 1 MHz | 3.00 | ASTM D150,IEC 60250 | |
| 50 Hz | 3.00 | IEC 60250 | |
| 60 Hz | 3.00 | IEC 60250 | |
| 耗散因數(shù) | |||
| 1 MHz | 0.013 | ASTM D150 | |
| 50 Hz | 2.0E-3 | IEC 60250 | |
| 60 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 1.3E-3 | IEC 60250 | |
| 耐電弧性12 | PLC 6 | ASTM D495 | |
| 相比耐漏電起痕指數(shù)(CTI) | PLC 3 | UL 746A | |
| 漏電起痕指數(shù) | IEC 60112 | ||
| -- | 200 | V | |
| 解決方案 B | 100 | V | |
| 高電弧燃燒指數(shù)(HAI)13 | PLC 0 | UL 746A | |
| 高壓電弧抗點(diǎn)燃指數(shù) (HVAR) (PLC) | PLC 3 | UL 746A | |
| 熱絲引燃 (HWI) | PLC 3 | UL 746A | |
| 可燃性 | 額定值 | 單位制 | 測(cè)試方法 |
| UL 阻燃等級(jí) | UL 94 | ||
| 0.75 mm | V-0 | ||
| 2.5 mm | 5VA | ||
| 灼熱絲易燃指數(shù)(1.0 mm) | 960 | ℃ | IEC 60695-2-12 |
| 熱燈絲點(diǎn)火溫度 | IEC 60695-2-13 | ||
| 1.0 mm | 825 | ℃ | |
| 2.0 mm | 725 | ℃ | |
| 3.0 mm | 700 | ℃ | |
| 極限氧指數(shù) | 30 | % | ISO 4589-2 |
| 充模分析 | 額定值 | 單位制 | 測(cè)試方法 |
| 熔體粘度(260℃,1500 sec^-1) | 310 | Pa·s | ISO 11443 |
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 110 到 120 | ℃ | |
| 干燥時(shí)間 | 2.0 到 4.0 | hr | |
| 建議的最大水分含量 | 0.020 | % | |
| 料斗溫度 | 40 到 60 | ℃ | |
| 料筒后部溫度 | 230 到 245 | ℃ | |
| 料筒中部溫度 | 240 到 255 | ℃ | |
| 料筒前部溫度 | 245 到 265 | ℃ | |
| 射嘴溫度 | 240 到 260 | ℃ | |
| 加工（熔體）溫度 | 250 到 270 | ℃ | |
| 模具溫度 | 40 到 100 | ℃ | |
| 備注 1Tensile Bar 250 mm/min 3類(lèi)型 1,50 mm/min 41.3 mm/min 52.0 mm/min 6at Yield 780*10*4 sp=62mm 880*10*4 mm 9120*10*4 mm 10速率 A (50℃/h),壓 力1 (10N) 11速率 A (50℃/h),載荷2 (50N) 12鎢電極 13Surface |
|||
The VALOX family of thermoplastic polyester resins are semi-crystalline materials based on polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) polymers. VALOX resin formulations include many performance-matched grades designed to provide application-specific property profiles. VALOX resins combine heat and chemical resistance, as well as outstanding electrical properties with exceptionally good processability and surface appearance.