Ultradur® S 4090 G4 BK15051
聚對(duì)苯二甲酸丁二酯+ASA (PBT+ASA)
德國巴斯夫-BASF Corporation
產(chǎn)品說明:
Ultradur S 4090 G4 BK15051 is a 20% glass reinforced, pigmented black PBT+ASA blend. It produces moldings with good surface finish, is resistant to chemicals and stress cracking, and has low shrinkage and warpage.
Applications
Applications include highly stressed equipment housings in the automotive, electrical and household sectors.
增強(qiáng)材料:玻璃纖維20%增強(qiáng)
材料特性:低翹曲,耐化學(xué)品良好,收縮性低,優(yōu)良外觀,Good ESCR (Stress Crack Resist.)
材料用途:電器外殼,家用貨品,汽車領(lǐng)域的應(yīng)用,外殼
加工方法:黑色粒子注射成型
供貨地區(qū):北美洲
中國代理:蘇州希普能工程塑料
Ultradur® S 4090 G4 BK15051巴斯夫中文加工參數(shù)表
物理性能 | 額定值 | 單位制 | 測試方法 |
密度 | 1.38 | g/cm³ | ISO 1183 |
熔融體積流量(MVR)(275℃/2.16kg) | 15 | cm³/10min | ISO 1133 |
吸水率 | ISO 62 | ||
飽和,23℃ | 0.40 | % | |
平衡,23℃,50% RH | 0.20 | % | |
Viscosity Number (Reduced Viscosity) | 108.0 | ml/g | ISO 1628 |
機(jī)械性能 | 額定值 | 單位制 | 測試方法 |
拉伸模量(23℃) | 7000 | MPa | ISO 527-1 |
拉伸應(yīng)力(斷裂,23℃) | 108 | MPa | ISO 527-2 |
拉伸應(yīng)變(斷裂,23℃) | 2.4 | % | ISO 527-2 |
彎曲模量(23℃) | 6400 | MPa | ISO 178 |
沖擊性能 | 額定值 | 單位制 | 測試方法 |
簡支梁缺口沖擊強(qiáng)度(23℃) | 7.0 | kJ/m² | ISO 179 |
熱性能 | 額定值 | 單位制 | 測試方法 |
載荷下熱變形溫度(1.8MPa,未退火) | 184 | ℃ | ISO 75-2/A |
溶融溫度(DSC) | 223 | ℃ | ISO 3146 |
線形熱膨脹系數(shù)-流動(dòng) | 4.0E-5 | cm/cm/℃ | |
注射 | 額定值 | 單位制 | |
干燥溫度 | 100 到 120 | ℃ | |
干燥時(shí)間 | 4.0 | hr | |
建議的最大水分含量 | 0.040 | % | |
加工(熔體)溫度 | 250 到 270 | ℃ | |
模具溫度 | 60 到 100 | ℃ | |
注塑壓力 | 3.50 到 12.5 | MPa | |
注射速度 | 快速 | ||
背壓 | < 1.00 | MPa |