Ultradur® S 4090 G4
聚對苯二甲酸丁二酯+ASA (PBT+ASA)
德國巴斯夫-BASF Corporation
產(chǎn)品說明:
Ultradur S 4090 G4 is a 20% glass reinforced PBT+ASA blend. It produces moldings with good surface finish, is resistant to chemicals and stress cracking, and has low shrinkage and warpage.
Applications
Applications include highly stressed equipment housings in the automotive, electrical and household sectors.
ul證書號：E41871-233617
增強(qiáng)材料：玻璃纖維20%增強(qiáng)
材料特性：低翹曲，耐化學(xué)品良好，收縮性低，優(yōu)良外觀，Good ESCR (Stress Crack Resist.)
材料用途：電器外殼，家用貨品，汽車領(lǐng)域的應(yīng)用，外殼
加工方法：粒子注射成型
供貨地區(qū)：北美洲，歐洲，亞太地區(qū)
中國代理：蘇州希普能工程塑料
Ultradur® S 4090 G4巴斯夫中文加工參數(shù)表
| 物理性能 | 額定值 | 單位制 | 測試方法 |
| 密度/比重 | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| 收縮率 | |||
| 流動:3.18 mm | 0.30 | % | |
| 垂直 | 0.74 | % | ISO 294-4 |
| 流動 | 0.43 | % | ISO 294-4 |
| 吸水率 | |||
| 飽和 | 0.40 | % | ASTM D570 |
| 飽和,23℃ | 0.40 | % | ISO 62 |
| 平衡,50% RH | 0.20 | % | ASTM D570 |
| 平衡,23℃,50% RH | 0.20 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 105.0 | ml/g | ISO 1628 |
| 機(jī)械性能 | 額定值 | 單位制 | 測試方法 |
| 拉伸模量 (23℃) | 6900 | MPa | ISO 527-1 |
| 抗張強(qiáng)度 | |||
| 斷裂,23℃ | 100 | MPa | ASTM D638, ISO 527-2 |
| 斷裂,-40℃ | 160 | MPa | ISO 527-2 |
| 斷裂,80℃ | 68.0 | MPa | ISO 527-2 |
| 斷裂,120℃ | 42.0 | MPa | ISO 527-2 |
| 斷裂,150℃ | 32.2 | MPa | ISO 527-2 |
| 伸長率 | |||
| 斷裂,23℃ | 2.5 | % | ASTM D638, ISO 527-2 |
| 斷裂,-40℃ | 2.7 | % | ISO 527-2 |
| 斷裂,80℃ | 4.2 | % | ISO 527-2 |
| 斷裂,120℃ | 7.4 | % | ISO 527-2 |
| 斷裂,150℃ | 6.7 | % | ISO 527-2 |
| 拉伸蠕變模量 | ISO 899-1 | ||
| 1 hr | 5300 | MPa | |
| 1000 hr | 4700 | MPa | |
| 彎曲模量 | |||
| 23℃ | 6100 | MPa | ASTM D790 |
| 23℃ | 6400 | MPa | ISO 178 |
| 彎曲強(qiáng)度 (23℃) | 159 | MPa | ASTM D790 |
| 沖擊性能 | 額定值 | 單位制 | 測試方法 |
| 簡支梁缺口沖擊強(qiáng)度 (23℃) | 7.0 | kJ/m² | ISO 179 |
| 簡支梁無缺口沖擊強(qiáng)度 | ISO 179 | ||
| -30℃ | 43 | kJ/m² | |
| 23℃ | 55 | kJ/m² | |
| 懸壁梁缺口沖擊強(qiáng)度 | |||
| -40℃ | 68 | J/m | ASTM D256 |
| 23℃ | 80 | J/m | ASTM D256 |
| 23℃ | 7.0 | kJ/m² | ISO 180 |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
| 載荷下熱變形溫度 | |||
| 0.45 MPa,未退火 | 216 | ℃ | ASTM D648 |
| 0.45 MPa,未退火 | 205 | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 194 | ℃ | ASTM D648 |
| 1.8 MPa,未退火 | 160 | ℃ | ISO 75-2/A |
| 熔融峰值溫度 | 223 | ℃ | ASTM D3418, ISO 3146 |
| 線形熱膨脹系數(shù)-流動 | 4.0E-5 | cm/cm/℃ | |
| RTI Elec | UL 746B | ||
| 0.71 mm | 130 | ℃ | |
| 1.5 mm | 130 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| RTI Imp | UL 746B | ||
| 0.71 mm | 90.0 | ℃ | |
| 1.5 mm | 90.0 | ℃ | |
| 3.0 mm | 90.0 | ℃ | |
| RTI | UL 746B | ||
| 0.71 mm | 130 | ℃ | |
| 1.5 mm | 130 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
| 表面電阻率 | |||
| 1.50 mm | 1.0E+14 | ohms | ASTM D257 |
| -- | 1.0E+14 | ohms | IEC 60093 |
| 體積電阻率 | |||
| 1.50 mm | > 1.0E+15 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| 介電常數(shù) | IEC 60250 | ||
| 100 Hz | 3.70 | ||
| 1 MHz | 3.60 | ||
| 耗散因數(shù) | IEC 60250 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 0.019 | ||
| 漏電起痕指數(shù) | 450 | V | IEC 60112 |
| 可燃性 | 額定值 | 單位制 | 測試方法 |
| UL 阻燃等級 | UL 94 | ||
| 0.71 mm | HB | ||
| 1.5 mm | HB | ||
| 3.0 mm | HB | ||
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 100 到 120 | ℃ | |
| 干燥時(shí)間 | 4.0 | hr | |
| 建議的最大水分含量 | 0.040 | % | |
| 加工（熔體）溫度 | 250 到 270 | ℃ | |
| 模具溫度 | 60 到 100 | ℃ | |
| 注塑壓力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 | ||
| 背壓 | < 1.00 | MPa | |