Ultramid® D3WG12 HMG BK00102
聚酰胺，未指定（尼龍，未指定)
德國巴斯夫-BASF Corporation
產(chǎn)品說明:
Ultramid D3WG12 HMG BK00102 is a 60% glass reinforced, injection molding polyamide offering high strength and stiffness. Due to inherently lower moisture absorption, Ultramid D3WG12 HMG BK00102 shows improved retention of mechanical properties after moisture conditioning. In addition, molded parts possess an exceptional surface finish.
Applications
Ultramid D3WG12 HMG BK00102 was designed for applications requiring very high rigidity and should be considered for components that are constructed with metal.
增強(qiáng)材料：玻璃纖維60%增強(qiáng)
材料特性：出色的外觀，高剛性，高強(qiáng)度
材料用途：金屬取代
加工方法：黑色粒子注射成型
供貨地區(qū)：北美洲，亞太地區(qū)
中國代理：蘇州希普能工程塑料
Ultramid® D3WG12 HMG BK00102 巴斯夫中文加工參數(shù)表
| 物理性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
| 密度 | 1.75 | -- | g/cm³ | ISO 1183 |
| 收縮率 | ISO 294-4 | |||
| 垂直 | 0.25 | -- | % | |
| 流動 | 0.19 | -- | % | |
| 吸水率 | ISO 62 | |||
| 飽和,23℃ | 2.5 | -- | % | |
| 平衡,23℃,50% RH | 1.0 | -- | % | |
| 機(jī)械性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
| 拉伸模量(23℃) | 20200 | 20800 | MPa | ISO 527-1 |
| 拉伸應(yīng)力(斷裂,23℃) | 248 | 220 | MPa | ISO 527-2 |
| 拉伸應(yīng)變(斷裂,23℃) | 2.5 | 2.2 | % | ISO 527-2 |
| 彎曲模量(23℃) | 18900 | 19400 | MPa | ISO 178 |
| 彎曲應(yīng)力(23℃) | 383 | 351 | MPa | ISO 178 |
| 沖擊性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
| 簡支梁缺口沖擊強(qiáng)度 | ISO 179 | |||
| -30℃ | 12 | 12 | kJ/m² | |
| 23℃ | 13 | 15 | kJ/m² | |
| 簡支梁無缺口沖擊強(qiáng)度 | ISO 179 | |||
| -30℃ | 95 | 85 | kJ/m² | |
| 23℃ | 99 | 93 | kJ/m² | |
| 懸壁梁缺口沖擊強(qiáng)度 | ISO 180 | |||
| -40℃ | 12 | 11 | kJ/m² | |
| 23℃ | 13 | 13 | kJ/m² | |
| 熱性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
| 載荷下熱變形溫度(1.8 MPa,未退火) | 224 | -- | ℃ | ISO 75-2/A |
| 溶融溫度（DSC） | 260 | -- | ℃ | ISO 3146 |
| 注射 | 干燥 | 單位制 | ||
| 干燥溫度 | 80 | ℃ | ||
| 干燥時間 | 2.0 到 4.0 | hr | ||
| 建議的最大水分含量 | 0.15 | % | ||
| 加工（熔體）溫度 | 280 到 305 | ℃ | ||
| 模具溫度 | 80 到 90 | ℃ | ||
| 注塑壓力 | 3.50 到 12.5 | MPa | ||
| 注射速度 | 快速 | |||