Ultramid® Advanced T1000 HG7 BK23593
聚酰胺 6T/6I（尼龍 6T/6I）PA6T
德國巴斯夫-BASF Corporation
產(chǎn)品說明:
Preliminary Product - Ultramid Advanced T1000 HG7 BK23593 is a heat stabilized, partially aromatic, 35% glassfiber reinforced polyphthalamide for injection molding with strong mechanical properties especially at elevated temperatures and excellent chemical resistance for highly stressed parts. This material has high strength and stiffness, very low water absorption and outstanding dimensional stability. It features a high melting point (320C) and excellent melt stability.
黃卡號(hào)碼：E41871-104037816
增強(qiáng)材料：玻璃纖維35%增強(qiáng)
含添加劑：熱穩(wěn)定劑
材料特性：芳香、高剛性、高強(qiáng)度、較高的熔體穩(wěn)定性、耐化學(xué)品性良好、熱穩(wěn)定、吸水低或不吸水、High Dimensional Stability
加工方法：粒子注射成型
供貨地區(qū)：歐洲、北美洲
中國代理：蘇州希普能工程塑料
Ultramid® Advanced T1000 HG7 BK23593 加工參數(shù)表
| 物理性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
| 密度 | 1.49 | -- | g/cm³ | ISO 1183 |
| 收縮率 | ISO 294-4 | |||
| 垂直 | 0.93 | -- | % | |
| 流動(dòng) | 0.40 | -- | % | |
| 機(jī)械性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
| 拉伸模量 | ISO 527-1 | |||
| 23℃ | 14000 | 14000 | MPa | |
| 80℃ | 12500 | 12000 | MPa | |
| 120℃ | 10000 | -- | MPa | |
| 拉伸應(yīng)力 | ISO 527-2 | |||
| 斷裂,23℃ | 220 | 210 | MPa | |
| 斷裂,80℃ | 180 | 145 | MPa | |
| 斷裂,120℃ | 135 | -- | MPa | |
| 拉伸應(yīng)變 | ISO 527-2 | |||
| 斷裂,23℃ | 2.0 | 1.9 | % | |
| 斷裂,80℃ | 2.0 | 2.2 | % | |
| 斷裂,120℃ | 2.9 | -- | % | |
| 沖擊性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
| 簡支梁缺口沖擊強(qiáng)度 | ISO 179 | |||
| -30℃ | 8.0 | -- | kJ/m² | |
| 23℃ | 8.0 | -- | kJ/m² | |
| 簡支梁無缺口沖擊強(qiáng)度 | ISO 179 | |||
| -30℃ | 70 | -- | kJ/m² | |
| 23℃ | 70 | -- | kJ/m² | |
| 熱性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
| 載荷下熱變形溫度(1.8 MPa,未退火) | 280 | -- | ℃ | ISO 75-2/A |
| 溶融溫度（DSC） | 320 | -- | ℃ | ISO 3146 |
| 注射 | 干燥 | 單位制 | ||
| 干燥溫度 - 熱風(fēng)干燥機(jī) | 120 | ℃ | ||
| 干燥時(shí)間 | 8.0 | hr | ||
| 建議的最大水分含量 | 0.050 | % | ||
| 加工（熔體）溫度 | 345 到 360 | ℃ | ||
| 模具溫度 | 150 到 170 | ℃ | ||