Ultraform® W 2320 003 UNC Q600
聚甲醛 (POM) 共聚物
德國巴斯夫-BASF Corporation
產(chǎn)品說明:
Ultraform W 2320 003 UNC Q600 is a very easy flowing and rapidly solidifying injection molding POM grade for use where processing is extremely difficult but mechanical properties are lower. Contains a mold release agent.
Typical applications include thin walled parts.
ul證書號：E36632-104392267
含添加劑：脫模劑
材料特性：良好的流動性，脫模性能良好
材料用途：薄壁部件
加工方法：顆粒注射成型
供貨地區(qū)：北美洲
中國代理：蘇州希普能工程塑料
Ultraform® W 2320 003 UNC Q600巴斯夫POM中文加工參數(shù)表
| 物理性能 | 額定值 | 單位制 | 測試方法 |
| 密度/比重 | 1.40 | g/cm³ | ASTM D792,ISO 1183 |
| 熔融體積流量（MVR）(190℃/2.16kg) | 25 | cm³/10min | ISO 1133 |
| 收縮率 | |||
| 流動:3.18 mm | 1.9 | % | |
| 垂直 | 2.1 | % | ISO 294-4 |
| 流動 | 2.0 | % | ISO 294-4 |
| 吸水率 | |||
| 飽和 | 0.80 | % | ASTM D570 |
| 飽和,23℃ | 0.80 | % | ISO 62 |
| 平衡,50% RH | 0.20 | % | ASTM D570 |
| 平衡,23℃,50% RH | 0.20 | % | ISO 62 |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
| 拉伸模量(23℃) | 2800 | MPa | ISO 527-1 |
| 抗張強度 | |||
| 屈服,23℃ | 65.0 | MPa | ASTM D638,ISO 527-2 |
| 屈服,-40℃ | 93.0 | MPa | ISO 527-2 |
| 屈服,80℃ | 33.0 | MPa | ISO 527-2 |
| 伸長率(屈服,23℃) | 7.5 | % | ASTM D638,ISO 527-2 |
| 標(biāo)稱拉伸斷裂應(yīng)變(23℃) | 24 | % | ISO 527-2 |
| 拉伸蠕變模量 | ISO 899-1 | ||
| 1 hr | 2100 | MPa | |
| 1000 hr | 1350 | MPa | |
| 彎曲模量(23℃) | 2760 | MPa | ASTM D790 |
| 沖擊性能 | 額定值 | 單位制 | 測試方法 |
| 簡支梁缺口沖擊強度 | ISO 179 | ||
| -30℃ | 4.0 | kJ/m² | |
| 23℃ | 5.0 | kJ/m² | |
| 簡支梁無缺口沖擊強度 | ISO 179 | ||
| -30℃ | 150 | kJ/m² | |
| 23℃ | 150 | kJ/m² | |
| 懸壁梁缺口沖擊強度 | ASTM D256 | ||
| -40℃ | 45 | J/m | |
| 23℃ | 55 | J/m | |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
| 載荷下熱變形溫度 | |||
| 0.45 MPa,未退火 | 154 | ℃ | ASTM D648 |
| 0.45 MPa,未退火 | 156 | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 99.0 | ℃ | ASTM D648 |
| 1.8 MPa,未退火 | 100 | ℃ | ISO 75-2/A |
| 熔融峰值溫度 | 167 | ℃ | ASTM D3418,ISO 3146 |
| 線形熱膨脹系數(shù)-流動 | |||
| -- | 6.0E-5 | cm/cm/℃ | ASTM E831 |
| -- | 1.1E-4 | cm/cm/℃ | |
| RTI Elec | UL 746B | ||
| 1.5 mm | 105 | ℃ | |
| 3.0 mm | 105 | ℃ | |
| RTI Imp | UL 746B | ||
| 1.5 mm | 90.0 | ℃ | |
| 3.0 mm | 90.0 | ℃ | |
| RTI | UL 746B | ||
| 1.5 mm | 90.0 | ℃ | |
| 3.0 mm | 105 | ℃ | |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
| 表面電阻率 | |||
| 1.50 mm | 1.0E+13 | ohms | ASTM D257 |
| -- | 1.0E+13 | ohms | IEC 60093 |
| 體積電阻率 | |||
| 1.50 mm | 1.0E+15 | ohms·cm | ASTM D257 |
| -- | 1.0E+15 | ohms·cm | IEC 60093 |
| 介電強度 | 40 | kV/mm | IEC 60243-1 |
| 介電常數(shù) | IEC 60250 | ||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.80 | ||
| 耗散因數(shù) | IEC 60250 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 5.0E-3 | ||
| 漏電起痕指數(shù) | 600 | V | IEC 60112 |
| 可燃性 | 額定值 | 單位制 | 測試方法 |
| UL 阻燃等級 | UL 94 | ||
| 1.5 mm | HB | ||
| 3.0 mm | HB | ||
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 80到110 | ℃ | |
| 干燥時間 | 2.0到4.0 | hr | |
| 建議的最大水分含量 | 0.15 | % | |
| 加工（熔體）溫度 | 190到230 | ℃ | |
| 模具溫度 | 60到120 | ℃ | |
| 注塑壓力 | 3.50到7.00 | MPa | |