Typical Application
Applications for Teflon ™ PFA 340 include extruded tubing and other profiles for hose, wire and cable insulation, and sleeving; industrial film; and injection or compression molded articles requiring superior electrical, chemical, and thermal properties.
Description
DuPont™ Teflon ® PFA 340 is a general-purpose fluoroplastic resin available in pellet form. Compared with other grades of Teflon ® PFA, its most unique features are a relatively high melt flow rate (typical MFR of 14) and properties that make it suitable for a variety of processes and demanding end uses. Table 1 shows the typical property data for Teflon ® PFA 340.
Teflon ® PFA 340 is used when traditional extrusion and molding processes are required for producing products with the superior properties of a fluoroplastic resin. Compared to other thermoplastics, the high melt strength and thermal stability of Teflon ® PFA 340 can be used to improve processing rates. Compared with other fluoroplastics, creep resistance at high service temperatures provides a superior balance and level of end-use properties. Teflon ® PFA 340 combines the processing ease of conventional thermoplastics with many properties similar to those of polytetrafluoroethylene.
Properly processed products made from neat Teflon ® PFA 340 resin provide the superior properties characteristic of fluoroplastic resins: chemical inertness, exceptional dielectric properties, heat resistance, toughness and flexibility, low coefficient of friction, non-stick characteristics, negligible moisture absorption, low flammability, performance at temperature extremes, and excellent weather resistance.
In a flame situation, products of Teflon ® PFA 340 resist ignition and do not promote flame spread. When ignited by flame from other sources, their contribution of heat is very small and added at a slow rate with very little smoke.
供貨地區(qū)：北美洲、拉丁美洲、歐洲、亞太地區(qū)
黃卡號(hào)碼：E54681-244681
材料特性：低摩擦系數(shù)、低吸濕性、低煙度、抗蠕變特性、良好的電氣性能、良好的熔體強(qiáng)度、良好的柔韌性、流動(dòng)高、耐候良好、耐化學(xué)品良好、耐熱中等、熱穩(wěn)定良好、韌性良好
材料用途：薄膜、電線電纜應(yīng)用、工業(yè)應(yīng)用、管道、管件、絕緣材料、型材
外觀形式：粒子
加工方法：擠出、樹(shù)脂傳遞成型、壓縮模塑、注射成型
物料性能：
| 物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 密度/比重 | 2.14 | g/cm³ | ASTM D792 |
| 熔流率（熔體流動(dòng)速率）(372℃/5.0 kg) | 14 | g/10 min | ASTM D3307,ISO 12086 |
| 吸水率(24 hr) | < 0.030 | % | ASTM D570 |
| 硬度 | 額定值 | 單位制 | 測(cè)試方法 |
| 肖氏硬度(邵氏 D) | 55 | ASTM D2240,ISO 868 | |
| 機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 抗張強(qiáng)度 | ASTM D3307,ISO 12086 | ||
| 23℃ | 24.8 | MPa | |
| 250℃ | 12.4 | MPa | |
| 伸長(zhǎng)率 | ASTM D3307,ISO 12086 | ||
| 斷裂,23℃ | 300 | % | |
| 斷裂,250℃ | 480 | % | |
| 彎曲模量 | ASTM D790,ISO 178 | ||
| 23℃ | 586 | MPa | |
| 250℃ | 55.2 | MPa | |
| 熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 連續(xù)使用溫度 | 260 | ℃ | |
| 熔融溫度 | 305 | ℃ | ASTM D4591 |
| 電氣性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 體積電阻率 | 1.0E+18 | ohms·cm | ASTM D257,ISO 1325 |
| 介電強(qiáng)度 | |||
| 0.250 mm,方法A（短時(shí)間） | 80 | kV/mm | ASTM D149 |
| 0.250 mm | 80 | kV/mm | IEC 60243-1 |
| 介電常數(shù)(1 MHz) | 2.03 | ASTM D150,IEC 60250 | |
| 耗散因數(shù)(1 MHz) | < 2.0E-4 | ASTM D150,IEC 60250 | |
| 可燃性 | 額定值 | 單位制 | 測(cè)試方法 |
| UL 阻燃等級(jí)1 | V-0 | UL 94 | |
| 極限氧指數(shù) | > 95 | % | ASTM D2863,ISO 4589-2 |
| 補(bǔ)充信息 | 額定值 | 單位制 | 測(cè)試方法 |
| Critical Shear Rate(372℃) | 50.0 | sec^-1 | |
| MIT Folding Endurance2(200.0 µm) | 1.5E+4 | Cycles | ASTM D2176 |
| 備注 1These results are based on laboratory tests under controlled conditions and do not reflect performance under actual fire conditions,current rating is a typical theoretical value. 2Depending on fabrication conditions |
|||
扎根于過(guò)去。放眼于未來(lái)。
Teflon™ PFA 是一種四氟乙烯-全氟烷氧基醚共聚物樹(shù)脂，可以提供顆粒狀和粉末狀兩種產(chǎn)品形態(tài)。這種氟聚合物樹(shù)脂可以改進(jìn)很多行業(yè)（包括化學(xué)加工、電子、半導(dǎo)體、制藥和生物技術(shù)領(lǐng)域）生產(chǎn)的產(chǎn)品。
Teflon™ PFA 樹(shù)脂的特性和優(yōu)勢(shì)
Teflon™ PFA 樹(shù)脂可以用傳統(tǒng)的熱熔擠出工藝或注塑、壓塑、滾塑成型、傳遞成型和吹塑工藝進(jìn)行加工。Teflon™ PFA 樹(shù)脂的熔體強(qiáng)度和熱穩(wěn)定性很高，有利于采用較大的模具孔和高溫涂布工藝，從而提高加工速度。
這種樹(shù)脂結(jié)合了傳統(tǒng)熱塑性樹(shù)脂的易加工優(yōu)勢(shì)和 Teflon™ PTFE（聚四氟乙烯）的出色性能，包括：
? 出色的耐化學(xué)腐蝕性
? 卓越的電氣性能
? 高達(dá) 260℃ (500°F) 的連續(xù)工作溫度
? 強(qiáng)大的耐高溫蠕變性能
? 出色的低溫韌性
? 出色的阻燃性
Teflon™ PFA 產(chǎn)品系列
Teflon™ PFA 產(chǎn)品系列包括各種熔體流動(dòng)速率 (MFR) 的樹(shù)脂等級(jí)產(chǎn)品，這些產(chǎn)品適用于各種熱塑成型工藝，包括管和薄膜擠出成型、注塑、傳遞成型、壓塑成型和吹塑成型工藝。還可以提供用作涂層、薄膜或彌散材料的 PFA 產(chǎn)品。
Teflon™ PFA 300 系列
? Teflon™ PFA 300 系列樹(shù)脂是通用型 PFA 樹(shù)脂，適用于模壓或擠塑等熱塑性成型工藝
Teflon™ PFA 400HP 系列
? 完全氟化的 Teflon™ PFA 400HP 系列樹(shù)脂專(zhuān)為滿足化學(xué)流體處理行業(yè)對(duì)高純度和最小萃取量的要求而設(shè)計(jì)。
? Teflon™ PFA HP 氟聚合物樹(shù)脂制成的組件具有出色的耐化學(xué)腐蝕性和耐環(huán)境應(yīng)力開(kāi)裂性。這種樹(shù)脂幾乎不受任何化學(xué)品和溶劑的影響。
Teflon™ PFA 900HP Plus 系列
? Teflon™ PFA 900HP Plus 氟聚合物樹(shù)脂具有與 Teflon™ PFA HP 等級(jí)產(chǎn)品一樣出色的耐化學(xué)腐蝕性、高純度和防離子污染性能，并且具有更長(zhǎng)的抗撓曲壽命和更好的耐化學(xué)應(yīng)力開(kāi)裂性能。此外，這種樹(shù)脂還賦予產(chǎn)品更高透明度和更好的表面光潔度，便于觀察在水處理系統(tǒng)中的雜質(zhì)并防止微生物在表面積聚。
? 這種樹(shù)脂能夠提供更穩(wěn)定可靠，無(wú)雜質(zhì)污染以及耐含氟表面活性劑等特性，滿足于半導(dǎo)體制造加工過(guò)程中日益嚴(yán)苛的要求。