VALOX™ V3900WX
Generic Name: 聚碳酸酯+聚丁烯對(duì)苯二甲酸酯（PC+PBT） - 提供方: SABIC
VALOX V3900WX is an unreinforced, UV stabilized, weatherable, impact modified flame retardant Polybutylene Terephthalate/Polycarbonate (PBT) injection moldable grade. It has excellent chemical resistance and a UL94V0@1.5mm and 5VA@3.0mm flame rating. This is an excellent candidate for a wide variety of applications including outdoor enclosures requiring UL746C F1 weatherability performance.
黃卡號(hào)碼：E207780-498686
材料用途：3D打印機(jī)、草坪和園林設(shè)備、電氣/電子應(yīng)用領(lǐng)域、電器用具、電子顯示器、工業(yè)應(yīng)用、建筑應(yīng)用領(lǐng)域、軍事應(yīng)用、汽車(chē)配件、室外應(yīng)用、外科器械、液體處理、醫(yī)療/護(hù)理用品、醫(yī)療器械、照明應(yīng)用、Electric Vehicle (EV) Applications、Energy Storage、Heavy Transportation、Material Handling、Rail Applications、Water Management
外觀(guān)形式：粒子注射成型
供貨地區(qū)：亞太地區(qū)
物料性能：
| 物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 密度/比重 | 1.30 | g/cm³ | ASTM D792,ISO 1183 |
| 熔流率（熔體流動(dòng)速率）(266℃/5.0 kg) | 35 | g/10 min | ASTM D1238 |
| 熔融體積流量（MVR）(265℃/2.16 kg) | 11 | cm³/10min | ISO 1133 |
| 收縮率-流動(dòng)(3.20 mm) | 0.70 到 1.0 | % | 內(nèi)部方法 |
| 吸水率 | ISO 62 | ||
| 飽和,23℃ | 0.10 | % | |
| 平衡,23℃,50% RH | 0.030 | % | |
| 室外適用性 | f1 | UL 746C | |
| 機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 拉伸模量 | |||
| --1 | 2200 | MPa | ASTM D638 |
| -- | 2090 | MPa | ISO 527-1/1 |
| 抗張強(qiáng)度 | |||
| 屈服2 | 53.0 | MPa | ASTM D638 |
| 屈服 | 48.0 | MPa | 內(nèi)部方法 |
| 屈服 | 51.0 | MPa | ISO 527-2/50 |
| 斷裂2 | 43.0 | MPa | ASTM D638 |
| 斷裂 | 40.0 | MPa | ISO 527-2/50 |
| 伸長(zhǎng)率 | |||
| 屈服2 | 5.0 | % | ASTM D638 |
| 屈服 | 4.0 | % | ISO 527-2/50 |
| 斷裂2 | 50 | % | ASTM D638 |
| 斷裂 | 250 | % | 內(nèi)部方法 |
| 斷裂 | 42 | % | ISO 527-2/50 |
| 彎曲模量 | |||
| 50.0 mm 跨距3 | 2200 | MPa | ASTM D790 |
| --4 | 2130 | MPa | ISO 178 |
| 彎曲應(yīng)力 | |||
| --4,5 | 73.0 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距3 | 80.0 | MPa | ASTM D790 |
| 沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 簡(jiǎn)支梁缺口沖擊強(qiáng)度6(23℃) | 52 | kJ/m² | ISO 179/1eA |
| 懸壁梁缺口沖擊強(qiáng)度 | |||
| -30℃ | 110 | J/m | ASTM D256 |
| 23℃ | 800 | J/m | ASTM D256 |
| -30℃7 | 8.0 | kJ/m² | ISO 180/1A |
| 23℃7 | 45 | kJ/m² | ISO 180/1A |
| 裝有測(cè)量?jī)x表的落鏢沖擊 | ASTM D3763 | ||
| -40℃,Total Energy | 50.0 | J | |
| 23℃,Total Energy | 50.0 | J | |
| 熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 載荷下熱變形溫度 | |||
| 0.45 MPa,未退火,6.40 mm | 119 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,3.20 mm | 75.0 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,6.40 mm | 96.0 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,64.0 mm跨距7 | 77.0 | ℃ | ISO 75-2/Af |
| 維卡軟化溫度 | |||
| -- | 105 | ℃ | ASTM D15258 |
| -- | 123 | ℃ | ISO 306/B120 |
| -- | 121 | ℃ | ISO 306/B50 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 73 到 77℃ | 通過(guò) | ||
| 123 到 127℃ | 通過(guò) | ||
| 線(xiàn)形熱膨脹系數(shù) | ASTM E831,ISO 11359-2 | ||
| 流動(dòng):-40 到 40℃ | 8.8E-5 | cm/cm/℃ | |
| 垂直:-40 到 40℃ | 9.0E-5 | cm/cm/℃ | |
| RTI Elec | 120 | ℃ | UL 746B |
| RTI Imp | 120 | ℃ | UL 746B |
| RTI | 120 | ℃ | UL 746B |
| 可燃性 | 額定值 | 單位制 | 測(cè)試方法 |
| UL 阻燃等級(jí) | UL 94 | ||
| 1.5 mm | V-0 | ||
| 3.0 mm | 5VA | ||
| 灼熱絲易燃指數(shù) | IEC 60695-2-12 | ||
| 1.0 mm | 960 | ℃ | |
| 3.0 mm9 | 960 | ℃ | |
| 熱燈絲點(diǎn)火溫度 | IEC 60695-2-13 | ||
| 1.0 mm | 825 | ℃ | |
| 3.0 mm | 725 | ℃ | |
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 120 | ℃ | |
| 干燥時(shí)間 | 3.0 到 4.0 | hr | |
| 建議的最大水分含量 | 0.020 | % | |
| 建議注射量 | 40 到 80 | % | |
| 料筒后部溫度 | 240 到 255 | ℃ | |
| 料筒中部溫度 | 245 到 260 | ℃ | |
| 料筒前部溫度 | 250 到 265 | ℃ | |
| 射嘴溫度 | 245 到 260 | ℃ | |
| 加工（熔體）溫度 | 250 到 265 | ℃ | |
| 模具溫度 | 65 到 90 | ℃ | |
| 背壓 | 0.300 到 0.700 | MPa | |
| 螺桿轉(zhuǎn)速 | 50 到 80 | rpm | |
| 排氣孔深度 | 0.025 到 0.038 | mm | |
| 備注 15.0 mm/min 2類(lèi)型 1,50 mm/min 31.3 mm/min 42.0 mm/min 5at Yield 680*10*4 sp=62mm 780*10*4 mm 8速率 A (50°C/h),載荷2 (50N) 9by VDE |
|||
聚對(duì)苯二甲酸丁二醇酯，英文名polybutylene terephthalate（簡(jiǎn)稱(chēng)PBT），屬于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)與對(duì)苯二甲酸(PTA)或者對(duì)苯二甲酸酯(DMT)聚縮合而成，分子式為(C8H8·C4H6·C3H3N)x，并經(jīng)由混煉程序制成的乳白色半透明到不透明、結(jié)晶型熱塑性聚酯樹(shù)脂。與PET一起統(tǒng)稱(chēng)為熱塑性聚酯，或飽和聚酯。PBT是最堅(jiān)韌的工程熱塑材料之一，它是半結(jié)晶材料，有非常好的化學(xué)穩(wěn)定性、機(jī)械強(qiáng)度、電絕緣特性和熱穩(wěn)定性。