Ultradur® B 4406 G4
聚丁烯對(duì)苯二甲酸酯(PBT)
德國(guó)巴斯夫-BASF Corporation
產(chǎn)品說(shuō)明:
Ultradur B 4406 G4 is an injection molding grade with 20 % glass fibers for parts requiring enhanced fire resistance (eg relay housings, plug-and-socket connectors, switches, lighting components).
Applications
Typical applications include relay housings, plug-and-socket connectors, switches, and lighting components.
ul證書(shū)號(hào)：E41871-233788，E41871-233789，E36632-100378527
增強(qiáng)材料：玻璃纖維20%增強(qiáng)
材料特性：阻燃
材料用途：開(kāi)關(guān)，連接器，外殼，照明應(yīng)用
加工方法：粒子注射成型
供貨地區(qū)：亞太地區(qū)，歐洲，北美洲
中國(guó)代理：蘇州希普能工程塑料
Ultradur® B 4406 G4巴斯夫中文加工參數(shù)表
| 物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 密度/比重 | 1.55 | g/cm³ | ASTM D792,ISO 1183 |
| 熔融體積流量（MVR）(250℃/2.16kg) | 11 | cm³/10min | ISO 1133 |
| 收縮率-流動(dòng)(3.18 mm) | 0.30 | % | |
| 吸水率 | |||
| 飽和 | 0.40 | % | ASTM D570 |
| 飽和,23℃ | 0.40 | % | ISO 62 |
| 平衡,50% RH | 0.20 | % | ASTM D570 |
| 平衡,23℃,50% RH | 0.20 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 112.0 | ml/g | ISO 1628 |
| 機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 拉伸模量(23℃) | 8200 | MPa | ISO 527-1 |
| 抗張強(qiáng)度 | |||
| 斷裂,23℃ | 117 | MPa | ASTM D638 |
| 斷裂,23℃ | 125 | MPa | ISO 527-2 |
| 伸長(zhǎng)率 | |||
| 斷裂,23℃ | 2.2 | % | ASTM D638 |
| 斷裂,23℃ | 2.6 | % | ISO 527-2 |
| 沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 簡(jiǎn)支梁缺口沖擊強(qiáng)度(23℃) | 9.0 | kJ/m² | ISO 179 |
| 簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度(23℃) | 48 | kJ/m² | ISO 179 |
| 懸壁梁缺口沖擊強(qiáng)度(23℃) | 53 | J/m | ASTM D256 |
| 熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 載荷下熱變形溫度 | |||
| 0.45 MPa,未退火 | 215 | ℃ | ASTM D648 |
| 0.45 MPa,未退火 | 223 | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 177 | ℃ | ASTM D648 |
| 1.8 MPa,未退火 | 200 | ℃ | ISO 75-2/A |
| 熔融峰值溫度 | 223 | ℃ | ASTM D3418,ISO 3146 |
| 線(xiàn)形熱膨脹系數(shù)-流動(dòng) | |||
| -- | 3.0E-5 | cm/cm/℃ | ASTM E831 |
| -- | 5.0E-5 | cm/cm/℃ | |
| RTI Elec | UL 746B | ||
| 0.75 mm | 140 | ℃ | |
| 1.5 mm | 140 | ℃ | |
| 3.0 mm | 140 | ℃ | |
| RTI Imp | UL 746B | ||
| 0.75 mm | 120 | ℃ | |
| 1.5 mm | 120 | ℃ | |
| 3.0 mm | 120 | ℃ | |
| RTI | UL 746B | ||
| 0.75 mm | 125 | ℃ | |
| 1.5 mm | 130 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| 電氣性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 體積電阻率 | |||
| 1.50 mm | > 1.0E+15 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| 介電常數(shù) | IEC 60250 | ||
| 100 Hz | 3.90 | ||
| 1 MHz | 3.60 | ||
| 耗散因數(shù) | IEC 60250 | ||
| 100 Hz | 7.0E-3 | ||
| 1 MHz | 0.017 | ||
| 漏電起痕指數(shù) | 200 | V | IEC 60112 |
| 可燃性 | 額定值 | 單位制 | 測(cè)試方法 |
| UL 阻燃等級(jí) | UL 94 | ||
| 0.40 mm | V-0 | ||
| 0.75 mm | V-0 | ||
| 1.5 mm | V-0 | ||
| 3.0 mm | V-0 | ||
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 100到120 | ℃ | |
| 干燥時(shí)間 | 4.0 | hr | |
| 建議的最大水分含量 | 0.040 | % | |
| 加工（熔體）溫度 | 250到270 | ℃ | |
| 模具溫度 | 60到100 | ℃ | |
| 注塑壓力 | 3.50到12.5 | MPa | |
| 注射速度 | 快速 | ||
| 背壓 | < 1.00 | MPa | |