Ultradur® B 4040 G3 FR BK7696
聚對(duì)苯二甲酸丁二酯+PET (PBT+PET)
德國(guó)巴斯夫-BASF Corporation
產(chǎn)品說明:
Ultradur B 4040 G3 FR BK7696 is a 15% glass filled, pigmented black, injection molding, flame retarded PBT+PET product. The product is intended for house hold appliances where good chemical resistance, heat resistance and flame retardancy are required. The product also exhibits good surface appearance.
Applications
Applications include oven and range top components, exterior parts for deep fryers, toasters, coffee machines, steam irons and cooker knobs and handles.
黃卡號(hào)碼：E36632-638785
增強(qiáng)材料：玻璃纖維15%增強(qiáng)
材料特性：耐化學(xué)品良好，耐熱良好，優(yōu)良外觀，阻燃
材料用途：電器用具
加工方法：黑色粒子注射成型
供貨地區(qū)：北美洲
中國(guó)代理：蘇州希普能工程塑料
Ultradur® B 4040 G3 FR BK7696 巴斯夫中文加工參數(shù)表
| 物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 密度 | 1.56 | g/cm³ | ISO 1183 |
| 熔融體積流量（MVR）(265℃/2.16kg) | 28 | cm³/10min | ISO 1133 |
| 機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 拉伸模量(23℃) | 7000 | MPa | ISO 527-1 |
| 拉伸應(yīng)力(斷裂,23℃) | 87.0 | MPa | ISO 527-2 |
| 拉伸應(yīng)變(斷裂,23℃) | 1.5 | % | ISO 527-2 |
| 彎曲模量(23℃) | 6800 | MPa | ISO 178 |
| 沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 簡(jiǎn)支梁缺口沖擊強(qiáng)度(23℃) | 5.0 | kJ/m² | ISO 179 |
| 簡(jiǎn)支梁無缺口沖擊強(qiáng)度(23℃) | 22 | kJ/m² | ISO 179 |
| 熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 載荷下熱變形溫度(1.8 MPa,未退火) | 157 | ℃ | ISO 75-2/A |
| 溶融溫度（DSC） | 220 | ℃ | ISO 3146 |
| RTI Elec | UL 746B | ||
| 1.5 mm | 140 | ℃ | |
| 3.0 mm | 140 | ℃ | |
| RTI Imp | UL 746B | ||
| 1.5 mm | 130 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| RTI | UL 746B | ||
| 1.5 mm | 130 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| 可燃性 | 額定值 | 單位制 | 測(cè)試方法 |
| UL 阻燃等級(jí) | UL 94 | ||
| 1.5 mm | V-0 | ||
| 5VA | |||
| 3.0 mm | V-0 | ||
| 5VA | |||
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 100 到 120 | ℃ | |
| 干燥時(shí)間 | 4.0 | hr | |
| 建議的最大水分含量 | 0.015 | % | |
| 加工（熔體）溫度 | 240 到 275 | ℃ | |
| 模具溫度 | 60 到 100 | ℃ | |
| 注塑壓力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 | ||
| 背壓 | < 1.00 | MPa | |