Ultramid® A3WG6 BK00564
聚酰胺 66 （尼龍66）PA66
德國(guó)巴斯夫-BASF Corporation
產(chǎn)品說明:
Ultramid A3WG6 BK00564 is a 30% glass fiber reinforced, pigmented black and heat resistance injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. A3EG6 is the preferred grade for producing electrically insulating parts.
Applications
Typical applications include lamp socket housings, cooling fans, insulating profiles for aluminum window frames, water containers for automotive cooling systems.
黃卡號(hào)碼：E36632-531632、E41871-233745、E41871-101468834
增強(qiáng)材料：玻璃纖維30%增強(qiáng)
材料特性：高剛性、耐熱良好、耐油、High Dimensional Stability
材料用途：機(jī)器/機(jī)械部件、汽車領(lǐng)域的應(yīng)用、容器、外殼
加工方法：黑色粒子注射成型
供貨地區(qū)：北美洲
中國(guó)代理：蘇州希普能工程塑料
Ultramid® A3WG6 BK00564 加工參數(shù)表
| 物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 密度 | 1.36 | g/cm³ | ISO 1183 |
| 吸水率 | ISO 62 | ||
| 飽和,23℃ | 5.5 | % | |
| 平衡,23℃,50% RH | 1.7 | % | |
| 機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 拉伸應(yīng)力(斷裂,23℃) | 179 | MPa | ISO 527-2 |
| 拉伸應(yīng)變(斷裂,23℃) | 2.6 | % | ISO 527-2 |
| 彎曲模量(23℃) | 8730 | MPa | ISO 178 |
| 沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 懸壁梁缺口沖擊強(qiáng)度(23℃) | 8.5 | kJ/m² | ISO 180 |
| 熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 載荷下熱變形溫度(1.8 MPa,未退火) | 250 | ℃ | ISO 75-2/A |
| 溶融溫度（DSC） | 260 | ℃ | ISO 3146 |
| RTI Elec | UL 746B | ||
| 0.71 mm | 125 | ℃ | |
| 1.5 mm | 125 | ℃ | |
| 3.0 mm | 125 | ℃ | |
| RTI Imp | UL 746B | ||
| 1.5 mm | 115 | ℃ | |
| 3.0 mm | 120 | ℃ | |
| RTI | UL 746B | ||
| 1.5 mm | 115 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| 可燃性 | 額定值 | 單位制 | 測(cè)試方法 |
| UL 阻燃等級(jí) | UL 94 | ||
| 0.71 mm | HB | ||
| 1.5 mm | HB | ||
| 3.0 mm | HB | ||
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 80 | ℃ | |
| 干燥時(shí)間 | 2.0 到 4.0 | hr | |
| 建議的最大水分含量 | 0.15 | % | |
| 加工（熔體）溫度 | 280 到 305 | ℃ | |
| 模具溫度 | 80 到 90 | ℃ | |
| 注塑壓力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 | ||