Ultramid® B3WM8 BK00102
聚酰胺6（尼龍6）PA6
德國巴斯夫-BASF Corporation
產(chǎn)品說明:
Ultramid B3WM8 BK00102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low warp and resistance to sink-mark formation. It maintains its inherent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid B3WM8 BK00102 is generally recommended for applications such as marine hardware, brackets, fittings, bobbins, office furniture, appliance components, and power tool housings.
增強材料：礦物40%填充
含添加劑：熱穩(wěn)定劑
材料特性：低翹曲、高剛性、耐化學品良好、高耐熱、耐碳氫化合物、耐油脂、優(yōu)異的加工性能、High Dimensional Stability
材料用途：船舶應用、動力/其它工具、家電部件、家具、配件、外殼、線軸
加工方法：黑色粒子注射成型
供貨地區(qū)：北美洲
中國代理：蘇州希普能工程塑料
Ultramid® B3WM8 BK00102巴斯夫中文加工參數(shù)表
| 物理性能 | 干燥 | 調節(jié)后的 | 單位制 | 測試方法 |
| 密度/比重 | 1.49 | -- | g/cm³ | ASTM D792,ISO 1183 |
| 吸水率 | ||||
| 24 hr | 1.1 | -- | % | ASTM D570 |
| 24 hr,23℃ | 1.1 | -- | % | ISO 62 |
| 飽和 | 5.7 | -- | % | ASTM D570 |
| 飽和,23℃ | 5.7 | -- | % | ISO 62 |
| 平衡,50% RH | 1.6 | -- | % | ASTM D570 |
| 平衡,23℃,50% RH | 1.6 | -- | % | ISO 62 |
| 機械性能 | 干燥 | 調節(jié)后的 | 單位制 | 測試方法 |
| 拉伸模量 | ISO 527-1 | |||
| -40℃ | 8310 | 7700 | MPa | |
| 23℃ | 6400 | 3800 | MPa | |
| 80℃ | 1360 | 1400 | MPa | |
| 120℃ | 970 | 1200 | MPa | |
| 150℃ | 910 | 840 | MPa | |
| 拉伸應力 | ISO 527-2 | |||
| 斷裂,-40℃ | 135 | 135 | MPa | |
| 斷裂,23℃ | 85.0 | 60.0 | MPa | |
| 斷裂,80℃ | 40.0 | 35.0 | MPa | |
| 斷裂,120℃ | 30.0 | 27.0 | MPa | |
| 斷裂,150℃ | 20.0 | 20.0 | MPa | |
| 拉伸應變 | ISO 527-2 | |||
| 斷裂,-40℃ | 6.0 | 5.0 | % | |
| 斷裂,23℃ | 10 | 30 | % | |
| 斷裂,80℃ | 35 | 30 | % | |
| 斷裂,120℃ | 40 | 40 | % | |
| 斷裂,150℃ | 40 | 60 | % | |
| 彎曲模量(23℃) | 5200 | 2100 | MPa | ISO 178 |
| 彎曲應力(23℃) | 140 | 50.0 | MPa | ISO 178 |
| 沖擊性能 | 干燥 | 調節(jié)后的 | 單位制 | 測試方法 |
| 簡支梁缺口沖擊強度(23℃) | 3.0 | -- | kJ/m² | ISO 179 |
| 簡支梁無缺口沖擊強度(23℃) | 130 | -- | kJ/m² | ISO 179 |
| 懸壁梁缺口沖擊強度(23℃) | 6.0 | -- | kJ/m² | ISO 180 |
| 熱性能 | 干燥 | 調節(jié)后的 | 單位制 | 測試方法 |
| 載荷下熱變形溫度 | ||||
| 0.45 MPa,未退火 | 190 | -- | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 90.0 | -- | ℃ | ISO 75-2/A |
| 熔融峰值溫度 | 220 | -- | ℃ | ASTM D3418,ISO 3146 |
| 電氣性能 | 干燥 | 調節(jié)后的 | 單位制 | 測試方法 |
| 體積電阻率 | ||||
| 1.50 mm | > 1.0E+15 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| 注射 | 干燥 | 單位制 | ||
| 干燥溫度 | 83 | ℃ | ||
| 干燥時間 | 2.0 到 4.0 | hr | ||
| 建議的最大水分含量 | 0.15 | % | ||
| 加工（熔體）溫度 | 270 到 295 | ℃ | ||
| 模具溫度 | 80 到 95 | ℃ | ||
| 注塑壓力 | 3.50 到 12.5 | MPa | ||
| 注射速度 | 快速 | |||