NORYL GTX™ GTX678
聚苯醚+PS+尼龍
SABIC
產(chǎn)品說明:
NORYL GTX678 resin is a conductive, high performance non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade is optimized for primer-less electrostatic and powder coat painting, and it is UL 5VA rated with a non-brominated, non-chlorinated FR package. NORYL GTX678 resin exhibits an excellent balance of conductivity, high heat resistance, good ductility, and is heat stabilized. This material is an excellent candidate for non-automotive painted applications such as office furniture, PVC/metal replacement, lighting ballast housings / enclosures, and appliance exteriors.
含添加劑：沖擊改性劑、熱穩(wěn)定劑、阻燃
材料特性：Low Specific Gravity、尺寸穩(wěn)定性良好、沖擊改性、導電、低翹曲、低吸濕、高剛性、高強度、良好抗撞擊性、耐化學品、耐熱高、熱穩(wěn)定、收縮性低、水解穩(wěn)定、外觀良好、無鹵阻燃
材料用途：安全帽、電腦組件、電氣/電子應用領(lǐng)域、電器用具、建筑材料、手機、照明應用
加工方法：注射成型
供貨地區(qū)：亞太地區(qū)
| 物理性能 | 額定值 | 單位制 | 測試方法 |
| 密度/比重 | 1.12 | g/cm³ | ASTM D792,ISO 1183 |
| 熔流率（熔體流動速率）(300℃/5.0 kg) | 7.8 | g/10 min | ASTM D1238 |
| 熔融體積流量（MVR）(300℃/5.0 kg) | 7.0 | cm³/10min | ISO 1133 |
| 收縮率-流動(3.20 mm) | 1.3 到 1.5 | % | 內(nèi)部方法 |
| 吸水率 | ISO 62 | ||
| 飽和,23℃ | 4.0 | % | |
| 平衡,23℃,50% RH | 0.50 | % | |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
| 拉伸模量 | |||
| --1 | 2900 | MPa | ASTM D638 |
| -- | 2900 | MPa | ISO 527-1/1 |
| 抗張強度 | |||
| 屈服2 | 58.0 | MPa | ASTM D638 |
| 屈服 | 58.0 | MPa | ISO 527-2/50 |
| 斷裂2 | 52.0 | MPa | ASTM D638 |
| 斷裂 | 52.0 | MPa | ISO 527-2/50 |
| 伸長率 | |||
| 屈服2 | 7.0 | % | ASTM D638 |
| 屈服 | 7.0 | % | ISO 527-2/50 |
| 斷裂2 | 12 | % | ASTM D638 |
| 斷裂 | 12 | % | ISO 527-2/50 |
| 彎曲模量 | |||
| 50.0 mm 跨距3 | 2600 | MPa | ASTM D790 |
| --4 | 2600 | MPa | ISO 178 |
| 彎曲應力 | |||
| --4,5 | 95.0 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距3 | 95.0 | MPa | ASTM D790 |
| 沖擊性能 | 額定值 | 單位制 | 測試方法 |
| 簡支梁缺口沖擊強度6(23℃) | 12 | kJ/m² | ISO 179/1eA |
| 懸壁梁缺口沖擊強度 | |||
| -30℃ | 70 | J/m | ASTM D256 |
| 23℃ | 100 | J/m | ASTM D256 |
| -30℃7 | 7.0 | kJ/m² | ISO 180/1A |
| 23℃7 | 10 | kJ/m² | ISO 180/1A |
| 裝有測量儀表的落鏢沖擊(23℃,Total Energy) | 60.0 | J | ASTM D3763 |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
| 載荷下熱變形溫度 | |||
| 0.45 MPa,未退火,3.20 mm | 195 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,4.00 mm,64.0 mm 跨距7 | 191 | ℃ | ISO 75-2/Bf |
| 維卡軟化溫度 | |||
| -- | 198 | ℃ | ASTM D15258 |
| -- | 195 | ℃ | ISO 306/B120 |
| -- | 197 | ℃ | ISO 306/B50 |
| Ball Pressure Test(123 到 127℃) | 通過 | IEC 60695-10-2 | |
| 線形熱膨脹系數(shù) | |||
| 流動:-40 到 40℃ | 7.8E-5 | cm/cm/℃ | ASTM E831 |
| 流動:23 到 60℃ | 8.3E-5 | cm/cm/℃ | ISO 11359-2 |
| 垂直:-40 到 40℃ | 8.0E-5 | cm/cm/℃ | ASTM E831 |
| 垂直:23 到 60℃ | 8.5E-5 | cm/cm/℃ | ISO 11359-2 |
| 比熱 | 1400 | J/kg/℃ | ASTM C351 |
| 導熱系數(shù) | 0.20 | W/m/K | ASTM C177 |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
| 體積電阻率 | 4000 | ohms·cm | ASTM D257 |
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 95 到 105 | ℃ | |
| 干燥時間 | 3.0 到 4.0 | hr | |
| 建議的最大水分含量 | 0.070 | % | |
| 建議注射量 | 30 到 50 | % | |
| 料筒后部溫度 | 260 到 300 | ℃ | |
| 料筒中部溫度 | 265 到 300 | ℃ | |
| 料筒前部溫度 | 270 到 300 | ℃ | |
| 射嘴溫度 | 275 到 300 | ℃ | |
| 加工（熔體）溫度 | 275 到 300 | ℃ | |
| 模具溫度 | 65 到 95 | ℃ | |
| 背壓 | 0.300 到 1.40 | MPa | |
| 螺桿轉(zhuǎn)速 | 20 到 100 | rpm | |
| 排氣孔深度 | 0.013 到 0.038 | mm | |
| 注射說明 Drying Time (Cumulative): 8 hr Minimum Moisture Content: 0.02% 擠壓說明 Profile Extrusion Parameters Drying Temperature: 105 to 110℃ Drying Time: 8 hr Drying Time (Cumulative): 24 hr Maximum Moisture Content: 0.03% Barrel-Zone 1 Temperature: 245 to 260℃ Barrel-Zone 2 Temperature: 245 to 260℃ Barrel-Zone 3 Temperature: 245 to 260℃ Barrel-Zone 4 Temperature: 245 to 260℃ Adapter Temperature: 245 to 260℃ Die Temperature: 245 to 260℃ Melt Temperature: 245 to 260℃ Calibrator Temperature: 35 to 75℃ Water Bath Temperature: 40-50℃ 備注 15.0 mm/min 2類型 1,50 mm/min 31.3 mm/min 42.0 mm/min 5at Yield 680*10*4 sp=62mm 780*10*4 mm 8速率 A (50℃/h),載荷2 (50N) |
|||
NORYL™樹脂系列是建立在SABIC的基礎(chǔ)上的專有的聚苯醚(PPE)技術(shù)。
NORYL樹脂在注塑成型方面表現(xiàn)出廣泛的應用前景一系列杰出的特性應用于：水管理，汽車，電氣，太陽能，能源儲存，建筑和建筑，電器還有許多其他行業(yè)。
NORYL樹脂，它是由高抗沖擊聚苯乙烯(HIPS)，呈無定形特征。
NORYL GTX和NORYL PPX樹脂利用流動特性和耐化學性半結(jié)晶材料，同時添加好尺寸穩(wěn)定，吸濕性低
非晶態(tài)PPE具有低蠕變傾向技術(shù)。
noryl™系列樹脂
NORYL系列樹脂代表了SABIC創(chuàng)新的聚苯醚(PPE)的組合。高沖擊聚苯乙烯(HIPS)，聚丙烯(PP)，聚酰胺(PA)混合技術(shù)或熱塑性彈性體(TPE)，連同選定的添加劑和填料。
通過將兩種樹脂的強度按順序結(jié)合在一起，創(chuàng)造了這些混合物，從而增加了價值滿足關(guān)鍵要求，如耐化學性、模數(shù)和可加工性。
作為NORYL樹脂家族的基石，PPE提供了獨特的組合增強其通用性的屬性。
PPE的特點包括:
•非常低的水分吸收
•優(yōu)異的水解穩(wěn)定性/抗水解性
•長期尺寸穩(wěn)定性-即使在高溫，水，潮濕的環(huán)境
•在各種環(huán)境下保持機械性能;包括紫外線(UV)曝光
•非常低的比重
•低翹曲+低蠕變
•優(yōu)異的電絕緣性能，由于高介電強度
•良好的沖擊、拉伸強度和彎曲強度
•阻燃等級均為非溴化和非氯化
•高耐熱性允許具有成本效益，高溫性能
應用程序開發(fā)注意事項
NORYL™樹脂一直被認為是最終用途應用的材料選擇，例如水管理、醫(yī)療保健和汽車內(nèi)飾等行業(yè)接觸化學物質(zhì)和清潔劑是很常見的。這是最重要的應用程序開發(fā)和材料選擇的考慮因素是環(huán)境中的最終產(chǎn)品將被使用。這不僅包括暴露于溫度極端，還會受到天氣、紫外線、過度潮濕、溶劑等的影響化學物質(zhì)。
接觸化學物質(zhì)的影響
在許多行業(yè)中，最終用途應用程序都有可能暴露對無數(shù)的化學品和/或清潔劑。這種接觸可能導致:
•物理降解-應力開裂，開裂，軟化，腫脹，變色
•性能下降-化學品與聚合物的反應可能導致熱塑性塑料的機械性能或其它性能的喪失