Teflon® PFA 350
全氟烷氧基
The Chemours Company
產(chǎn)品說明:
For inventory control purposes, product name may be followed by an X.
Products labeled PFA 350 and PFA 350 X are eguivalent, and all information in this document is applicable to both.
Typical Application:
Applications for Teflon" PFA 350 include extruded tubing for use in handling aggressive fluids at high pressures; chemical linings for pipes used in the chemical processing industry; film for high flex service; and traditional extruded, injection-molded, or blow-molded articles reguiring the unigue performance of Teflon".
Description:
Teflonil PFA 350 is a general-purpose fluoroplastic resin available in pellet form. Compared with other grades of Teflon PFA, its most unigue features are a relatively low flow rate, greatly increased flex life, and enhanced resistance to environmental stress-cracking over both Teflonw PFA B40 and S45 (Teflon PEA 350 has a typical MlTfolding endurance of 500,000*, compared to that of 15,000 and 50,000 for Tefloni" PFA 340 and 345, respectively). Teflonw PFA B50 is preferred when extended service is reguired in hostile environments involving chemical, thermal, and mechanical stress. Table 1 shows the typical property data for Teflonl" PFA S50.
Teflon PFA 350 is used when traditional extrusion and molding processes are reguired for producing products with the superior properties of a fluoroplastic resin. Compared to other thermoplastics, the high melt strength and thermal stability of Teflon" PFA 350 can be used to improve processing rates. Compared with other fluoroplastics, creep resistance at high service temperatures provides a superior balance and level of end-use properties. Teflon" PFA 350 combines the processing ease of conventional thermoplastics with many properties similar to those of polytetrafluoroethylene.
Properly processed products made from neat Teflon PFA 350 resin provide the superior properties characteristic of fluoroplastic resins: chemical inertness, exceptional dielectric properties, heat resistance, toughness and flexibility, low coefficient of friction, non-stick characteristics, negligible moisture absorption, low flammability, performance at temperature extremes, and excellent weather resistance.
In a flame situation, products of Teflon PFA 350 resist ignition and do not promote flame spread. When ignited by flame from other sources, their contribution of heat is very small and added at a slow rate with very little smoke.
供貨地區(qū)：北美洲、拉丁美洲、歐洲、亞太地區(qū)
黃卡號碼：E54681-244681
材料特性：Good ESCR (Stress Crack Resist.)、低吸濕性、高熔體強(qiáng)度、抗蠕變特性、良好的加工性能、良好的柔韌性、流動(dòng)性低、耐候良好、耐熱良好、熱穩(wěn)定良好、韌性良好、通用、無粘性、阻燃
材料用途：薄膜、襯里、吹塑成型應(yīng)用、管件、通用
外觀形式：粒子
加工方法：吹塑成型、擠出、樹脂傳遞成型、壓縮模塑、注射成型
物料性能：
| 物理性能 | 額定值 | 單位制 | 測試方法 |
| 密度/比重 | 2.14 | g/cm³ | ASTM D792 |
| 熔流率（熔體流動(dòng)速率）(372℃/5.0 kg) | 2.0 | g/10 min | ASTM D3307,ISO 12086 |
| 吸水率(24 hr) | < 0.030 | % | ASTM D570 |
| 硬度 | 額定值 | 單位制 | 測試方法 |
| 肖氏硬度(邵氏 D) | 55 | ASTM D2240,ISO 868 | |
| 機(jī)械性能 | 額定值 | 單位制 | 測試方法 |
| 抗張強(qiáng)度 | ASTM D3307,ISO 12086 | ||
| 23℃ | 27.6 | MPa | |
| 250℃ | 13.8 | MPa | |
| 伸長率 | ASTM D3307,ISO 12086 | ||
| 斷裂,23℃ | 300 | % | |
| 斷裂,250℃ | 500 | % | |
| 彎曲模量 | ASTM D790,ISO 178 | ||
| 23℃ | 517 | MPa | |
| 250℃ | 34.5 | MPa | |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
| 連續(xù)使用溫度 | 260 | ℃ | |
| 熔融溫度 | 305 | ℃ | ASTM D4591 |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
| 體積電阻率 | 1.0E+18 | ohms·cm | ASTM D257,ISO 1325 |
| 介電強(qiáng)度 | |||
| 0.250 mm,方法A（短時(shí)間） | 80 | kV/mm | ASTM D149 |
| 0.250 mm | 80 | kV/mm | IEC 60243-1 |
| 介電常數(shù)(1 MHz) | 2.03 | ASTM D150,IEC 60250 | |
| 耗散因數(shù)(1 MHz) | < 2.0E-4 | ASTM D150,IEC 60250 | |
| 可燃性 | 額定值 | 單位制 | 測試方法 |
| UL 阻燃等級1 | V-0 | UL 94 | |
| 極限氧指數(shù) | > 95 | % | ASTM D2863,ISO 4589-2 |
| 補(bǔ)充信息 | 額定值 | 單位制 | 測試方法 |
| Critical Shear Rate(372℃) | 12.0 | sec^-1 | |
| MIT Folding Endurance2(200.0 µm) | 5.0E+5 | Cycles | ASTM D2176 |
| 備注 1These results are based on laboratory tests under controlled conditions and do not reflect performance under actual fire conditions,current rating is a typical theoretical value. 2Depending on fabrication conditions |
|||
扎根于過去。放眼于未來。
Teflon™ PFA 是一種四氟乙烯-全氟烷氧基醚共聚物樹脂，可以提供顆粒狀和粉末狀兩種產(chǎn)品形態(tài)。這種氟聚合物樹脂可以改進(jìn)很多行業(yè)（包括化學(xué)加工、電子、半導(dǎo)體、制藥和生物技術(shù)領(lǐng)域）生產(chǎn)的產(chǎn)品。
Teflon™ PFA 樹脂的特性和優(yōu)勢
Teflon™ PFA 樹脂可以用傳統(tǒng)的熱熔擠出工藝或注塑、壓塑、滾塑成型、傳遞成型和吹塑工藝進(jìn)行加工。Teflon™ PFA 樹脂的熔體強(qiáng)度和熱穩(wěn)定性很高，有利于采用較大的模具孔和高溫涂布工藝，從而提高加工速度。
這種樹脂結(jié)合了傳統(tǒng)熱塑性樹脂的易加工優(yōu)勢和 Teflon™ PTFE（聚四氟乙烯）的出色性能，包括：
? 出色的耐化學(xué)腐蝕性
? 卓越的電氣性能
? 高達(dá) 260℃ (500°F) 的連續(xù)工作溫度
? 強(qiáng)大的耐高溫蠕變性能
? 出色的低溫韌性
? 出色的阻燃性
Teflon™ PFA 產(chǎn)品系列
Teflon™ PFA 產(chǎn)品系列包括各種熔體流動(dòng)速率 (MFR) 的樹脂等級產(chǎn)品，這些產(chǎn)品適用于各種熱塑成型工藝，包括管和薄膜擠出成型、注塑、傳遞成型、壓塑成型和吹塑成型工藝。還可以提供用作涂層、薄膜或彌散材料的 PFA 產(chǎn)品。
Teflon™ PFA 300 系列
? Teflon™ PFA 300 系列樹脂是通用型 PFA 樹脂，適用于模壓或擠塑等熱塑性成型工藝
Teflon™ PFA 400HP 系列
? 完全氟化的 Teflon™ PFA 400HP 系列樹脂專為滿足化學(xué)流體處理行業(yè)對高純度和最小萃取量的要求而設(shè)計(jì)。
? Teflon™ PFA HP 氟聚合物樹脂制成的組件具有出色的耐化學(xué)腐蝕性和耐環(huán)境應(yīng)力開裂性。這種樹脂幾乎不受任何化學(xué)品和溶劑的影響。
Teflon™ PFA 900HP Plus 系列
? Teflon™ PFA 900HP Plus 氟聚合物樹脂具有與 Teflon™ PFA HP 等級產(chǎn)品一樣出色的耐化學(xué)腐蝕性、高純度和防離子污染性能，并且具有更長的抗撓曲壽命和更好的耐化學(xué)應(yīng)力開裂性能。此外，這種樹脂還賦予產(chǎn)品更高透明度和更好的表面光潔度，便于觀察在水處理系統(tǒng)中的雜質(zhì)并防止微生物在表面積聚。
? 這種樹脂能夠提供更穩(wěn)定可靠，無雜質(zhì)污染以及耐含氟表面活性劑等特性，滿足于半導(dǎo)體制造加工過程中日益嚴(yán)苛的要求。