Ultramid? 8232G HS FR BK102
聚酰胺6
BASF Corporation
Product Description:
Ultramid 8232G HS FR BK102 is a 25% glass fiber reinforced, heat stabilized, flame retardant pigmented black PA6 injection molding compound exhibiting excellent melt stability characteristics. It combines flame retardant ability with an excellent balance of high strength, stiffness and heat distortion temperature.
Applications
Ultramid 8232G HS FR BK102 is generally recommended for applications such as connectors, terminal blocks, switches and receptacles, coil bobbins, and appliance housings.
黃卡號(hào)碼:E36632-231124
填料增強(qiáng):玻璃纖維增強(qiáng)材料,25%填料按重量
有添加劑:熱穩(wěn)定劑
粒料特性:高剛性、高強(qiáng)度、較高的熔體穩(wěn)定性、熱穩(wěn)定、阻燃
粒料用途:家電部件、開關(guān)、連接器、外殼、線軸
外觀顏色:黑色粒子
加工方法:注射成型
供貨地區(qū):北美洲
物料參數(shù)
物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
密度 / 比重 | 1.67 | g/cm3 | ASTM D792,ISO 1183 |
收縮率 - 流動(dòng)(3.18 mm) | 0.30 | % | |
吸水率 | |||
飽和 | 4.0 | % | ASTM D570 |
飽和,23℃ | 4.0 | % | ISO 62 |
平衡,50% RH | 1.1 | % | ASTM D570 |
平衡,23℃,50% RH | 1.1 | % | ISO 62 |
硬度 | 額定值 | 單位制 | 測(cè)試方法 |
洛氏硬度(R 級(jí)) | 121 | ASTM D785 | |
機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
拉伸模量(23℃) | 11000 | MPa | ISO 527-2 |
抗張強(qiáng)度(斷裂,23℃) | 150 | MPa | ASTM D638,ISO 527-2 |
伸長(zhǎng)率(斷裂,23℃) | 1.9 | % | ASTM D638,ISO 527-2 |
彎曲模量(23℃) | 10400 | MPa | ASTM D790,ISO 178 |
沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 | ISO 179 | ||
-30℃ | 8.0 | kJ/m2 | |
23℃ | 9.4 | kJ/m2 | |
簡(jiǎn)支梁無缺口沖擊強(qiáng)度(23℃) | 50 | kJ/m2 | ISO 179 |
懸壁梁缺口沖擊強(qiáng)度 | |||
23℃ | 77 | J/m | ASTM D256 |
23℃ | 9.8 | kJ/m2 | ISO 180 |
熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
載荷下熱變形溫度 | |||
1.8 MPa,未退火 | 205 | ℃ | ASTM D648 |
1.8 MPa,未退火 | 195 | ℃ | ISO 75-2/A |
熔融峰值溫度 | 220 | ℃ | ASTM D3418,ISO 3146 |
RTI Elec | UL 746 | ||
0.75 mm | 130 | ℃ | |
1.5 mm | 130 | ℃ | |
2.5 mm | 130 | ℃ | |
3.0 mm | 130 | ℃ | |
RTI Imp | UL 746 | ||
0.75 mm | 105 | ℃ | |
1.5 mm | 115 | ℃ | |
2.5 mm | 115 | ℃ | |
3.0 mm | 115 | ℃ | |
RTI | UL 746 | ||
0.75 mm | 105 | ℃ | |
1.5 mm | 115 | ℃ | |
2.5 mm | 115 | ℃ | |
3.0 mm | 120 | ℃ | |
可燃性 | 額定值 | 測(cè)試方法 | |
UL 阻燃等級(jí) | UL 94 | ||
0.75 mm | V-0 | ||
1.5 mm | V-0 | ||
2.5 mm | V-0 | ||
5VA | |||
3.0 mm | V-0 | ||
5VA | |||
注射 | 額定值 | 單位制 | |
干燥溫度 | 80 | ℃ | |
干燥時(shí)間 | 2.0 到 4.0 | hr | |
建議的最大水分含量 | 0.15 | % | |
加工(熔體)溫度 | 250 到 290 | ℃ | |
模具溫度 | 80 到 95 | ℃ | |
注塑壓力 | 3.50 到 12.5 | MPa | |
注射速度 | 快速 |