Ultramid® A 60G1 V25 BLACK 2N
聚酰胺 66 （尼龍66）PA66-GF25 FR(40)
德國(guó)巴斯夫-BASF Corporation
Ultramid® A 60G1 V25 Black 2N is a polyamide 66 based on a non-halogenated flame retardant system, reinforced with 25% of glass fiber, heat stabilized, for injection moulding. This grade offers excellent flame retardancy properties (UL 94, 5VA, GWIT) combined with excellent processing, mechanical and electrical performance. It can withstand temperatures of 160°C for over 6000 hours and has a UL F1 rating for weatherability resistance at 0.8 mm. European Railways Certifications - EN 45545-2 HL3; European Railways Certifications - EN 45545-2 HL3
黃卡號(hào)碼：E507491-104288112、E507491-104288111
增強(qiáng)材料：玻璃纖維13%增強(qiáng)
含添加劑：熱穩(wěn)定劑、阻燃劑
材料特性：優(yōu)異的加工性能、良好的電氣性能、熱穩(wěn)定、阻燃
加工方法：黑色、無色粒子注射成型
供貨地區(qū)：北美洲、非洲和中東
中國(guó)代理：蘇州希普能工程塑料
Ultramid® A 60G1 V25 BLACK 2N 加工參數(shù)表
| 物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 密度 | 1.38 | g/cm³ | ISO 1183 |
| 室外適用性1(Black) | f1 | UL 746C | |
| 機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 拉伸模量 | 9400 | MPa | ISO 527-1 |
| 拉伸應(yīng)力(斷裂) | 130 | MPa | ISO 527-2 |
| 拉伸應(yīng)變(斷裂) | 2.0 | % | ISO 527-2 |
| 沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 簡(jiǎn)支梁無缺口沖擊強(qiáng)度(23℃) | 53 | kJ/m² | ISO 179/1eU |
| 熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 載荷下熱變形溫度 | |||
| 0.45 MPa,未退火 | 260 | ℃ | ASTM D648 |
| 1.8 MPa,未退火 | 246 | ℃ | ASTM D648 |
| 1.8 MPa,未退火 | 247 | ℃ | ISO 75-2/A |
| 熔融溫度 | 263 | ℃ | ISO 11357-3 |
| 電氣性能 | 額定值 | 單位制 | 測(cè)試方法 |
| 表面電阻率 | 2.0E+15 | ohms | IEC 62631-3-2 |
| 體積電阻率 | 6.0E+14 | ohms·m | IEC 62631-3-1 |
| 介電強(qiáng)度(0.800 mm) | 35 | kV/mm | IEC 60243-1 |
| 漏電起痕指數(shù)(解決方案 A) | 600 | V | IEC 60112 |
| 可燃性 | 額定值 | 單位制 | 測(cè)試方法 |
| UL 阻燃等級(jí) | |||
| 3.2 mm | V-0 | UL 94,IEC 60695-11-10,-20 | |
| 0.8 mm | V-0 | IEC 60695-11-10,-20 | |
| 1.6 mm | V-0 | IEC 60695-11-10,-20 | |
| 1.6 mm2 | 5VA | IEC 60695-11-10,-20 | |
| 灼熱絲易燃指數(shù) | IEC 60695-2-12 | ||
| 0.8 mm | 960 | ℃ | |
| 1.6 mm | 960 | ℃ | |
| 3.2 mm | 960 | ℃ | |
| 熱燈絲點(diǎn)火溫度 | IEC 60695-2-13 | ||
| 0.8 mm | 775 | ℃ | |
| 1.6 mm | 775 | ℃ | |
| 極限氧指數(shù) | 33 | % | ISO 4589-2 |
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 80 | ℃ | |
| 建議的最大水分含量 | 0.20 | % | |
| 料筒后部溫度 | 265 到 275 | ℃ | |
| 料筒中部溫度 | 265 到 275 | ℃ | |
| 料筒前部溫度 | 270 到 280 | ℃ | |
| 模具溫度 | 60 到 90 | ℃ | |
| 注射說明 The material is supplied in airtight bags,ready for use. In case that the virgin material has absorbed moisture,it must be dried with a dehumidified air drying equipment,dew Point mini -20℃. Recommended time 2-4h. Injection Advice: All reinforced,flame retardant compounds generate some level of abrasion/corrosion to the steel processing equipment. These issues may be magnified by using incorrect processing conditions (temperatures,residence time,moisture level ...) during the moulding process. Therefore,BASF SE recommends you adhere to the processing conditions detailed in this technical data sheet. For equipment that comes into contact with molten flame retardant compounds,BASF SE advises you to use a steel with high chromium and high carbon content (having a minimum concentration of 16% Chromium) to prevent corrosion and abrasion. For the correct reference of steel associated to flame retardant compounds' processing,please refer to your equipment manufacturers. In the case of high requirements on surface quality a mould temperature of up to 120℃ can be considered. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size,part geometry / design. 備注 10.4mm 25V |
|||