Ultramid® A3XZC3 ESD BK23187
聚酰胺66-尼龍PA66
德國巴斯夫-BASF Corporation
產(chǎn)品說明:
Ultramid® A3XZC3 ESD offers a wide range of properties that enable its use in ex-zones
An impact-modified, carbon fibre reinforced injection moulding grade with reduced surface resistivity. Flame retardance based on red phosphorus for components requiring enhanced toughness and special requirements on electrical properties.
-Electrostatic discharge
-Outstanding flammability properties
-Reduced surface resistivity
-Excellent mechanical properties
-Low density
•Lighter components with the same mechanical performance
•Potential cost savings
增強材料：碳纖維15%增強
材料特性：ESD（靜電放電），阻燃
材料用途：工業(yè)防暴產(chǎn)品
加工方法：黑色粒子注射成型
供貨地區(qū)：德國
中國代理：蘇州希普能工程塑料
Ultramid® A3XZC3 ESD BK23187巴斯夫中文加工參數(shù)表
| Properties | Test method | Unit | Values |
| 聚合物縮寫 | - | - | PA66-I CF15 FR(52) |
| 密度 | ISO 1183 | kg/m³ | 1190 |
| 熔體體積速率 MVR 300℃/10 kg | ISO 1133 | cm³/10min | 7 |
| Injection molding | Test method | Unit | Values |
| 熔融溫度范圍 | - | ℃ | 280-300 |
| 模具溫度范圍 | - | ℃ | 80-90 |
| Shrinkage | Test method | Unit | Values |
| 成型收縮率（平行） | ISO 294-4 | % | 0.5 |
| 成型收縮率（常態(tài)） | ISO 294-4 | % | 0.55 |
| 加工收縮,受限,縱向(TM=290℃,TW=80℃) 1 | - | % | 0.4 |
| 機械性能 | 測試標準 | 單位 | 數(shù)值 |
| 拉伸延伸率 | |||
| 標稱斷裂伸長率 | ISO 527-1/-2 | % | 4.0 |
| 拉伸模量 | ISO 527-1/-2 | Mpa | 10000 |
| 沖擊性能 | 測試標準 | 單位 | 數(shù)值 |
| 簡支梁缺口(Charpy Notched) | |||
| -30℃ (-22℉) | ISO 179/1eA | kJ/m² | 60 |
| 23℃ (73℉) | ISO 179/1eA | kJ/m² | 65 |
| 燃燒性能 | 測試標準 | 單位 | 數(shù)值 |
| UL 防火等級 | IEC 60695-11-10 | 1.6mm | V-0 |
| 灼熱絲可燃性指數(shù)(GWFI)1mm | IEC 60695-2-12 | ℃ | 960 |
| 電學性能 | 測試標準 | 單位 | 數(shù)值 |
| 表面電阻率 | IEC 62631-3-2 | Ohm | 1.00E+06 |
| Footnotes 1 Model housing with central sprue, measures of the base:107x47x1.5mm. |
|||