Teflon® FEP 9495
聚全氟乙烯-丙烯樹脂
The Chemours Company
產品說明:
For inventory control purposes, product name may be followed by an X.Products labeled FEP 9495 and FEP 9495 X are equivalent, and all information in this document is applicable to both.
Typical Applications
Applications for Teflon ™ FEP 9495 include small diameter, thin wall wire and cable insulation; industrial film; and intricate or thin wall parts made by injection molding.
Description
Teflon ™ FEP 9495 is a melt-processible fluoroplastic resin available in pellet form. It is a copolymer of tetrafluoroethylene and hexafluoropropylene, without additives, that meets the requirements of ASTM D 2116 Type II. With a relatively high melt flow rate and excellent electrical properties, Teflon ™ FEP 9495 has been specifically designed for high-speed extrusion of thin coatings on small-gauge wires for twisted-pair constructions. Table 1 shows the typical property data for Teflon ™ FEP 9495.
As shown in Table 1, this resin provides the electrical and mechanical properties needed for low voltage applications. In addition, Teflon ™ FEP 9495 has a higher melt flow rate than most other fluoroplastic resins. This permits higher extrusion speeds and easier processing, making Teflon ™ FEP 9495 a cost-effective alternative for producing thin-wall extrusions.
Teflon ™ FEP 9495 is designed and made to have improved adhesion to copper wire under specific wireline process conditions, low dissipation factor at high frequencies, and significant plate-out resistance in melt extrusion. It is suitable as a solid insulator and as a foamed insulator, when used with an appropriate nucleant in a nitrogen gas injection process.
Teflon ™ FEP 9495 is used when traditional extrusion and molding processes are required for producing products with the superior properties of a fluoroplastic resin. Compared to other thermoplastics, the high melt strength and thermal stability of Teflon ™ FEP 9495 can be used to improve processing rates. Compared with other fluoroplastics, creep resistance at high service temperatures provides a superior balance and level of end-use properties. Teflon ™ FEP 9495 combines the processing ease of conventional thermoplastics with many properties similar to those of polytetrafluoroethylene.
Properly processed products made from neat Teflon ™ FEP 9495 resin provide the superior properties characteristic of fluoroplastic resins: chemical inertness, exceptional dielectric properties, heat resistance, toughness and flexibility, low coefficient of friction, non-stick characteristics, negligible moisture absorption, low flammability, performance at temperature extremes, and excellent weather resistance.In a flame situation, products of Teflon ™ FEP 9495 resist ignition and do not promote flame spread. When ignited by flame from other sources, their contribution of heat is very small and added at a slow rate with very little smoke.
供貨地區(qū)：北美洲、拉丁美洲、歐洲、亞太地區(qū)
黃卡號碼：E54681-639801
材料特性：低摩擦系數、低吸濕性、良好的電氣性能、良好的柔韌性、耐候性良好、耐化學品性能良好、耐熱性高、韌性良好、無粘性
材料用途：薄壁絕緣、低壓絕緣、電線電纜應用、通信電線絕緣材料
外觀形式：粒子
加工方法：電線&線纜擠出成型、擠出
物料性能：
| 物理性能 | 額定值 | 單位制 | 測試方法 |
| 密度/比重 | |||
| -- | 2.14 | g/cm³ | ASTM D792 |
| -- | 2.15 | g/cm³ | ISO 1183 |
| 熔流率（熔體流動速率）(372℃/5.0 kg) | 30 | g/10 min | ASTM D2116,ISO 12086 |
| 吸水率(24 hr) | < 0.010 | % | ASTM D570 |
| 硬度 | 額定值 | 單位制 | 測試方法 |
| 肖氏硬度(邵氏 D) | 55 | ASTM D2240,ISO 868 | |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
| 抗張強度(23℃) | 20.7 | MPa | ASTM D638,ISO 12086 |
| 伸長率(斷裂,23℃) | 300 | % | ASTM D638,ISO 12086 |
| 彎曲模量(23℃) | 521 | MPa | ASTM D790,ISO 178 |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
| 熔融峰值溫度 | 255 | ℃ | ASTM D4591 |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
| 介電強度(0.250 mm) | 80 | kV/mm | ASTM D149,IEC 243 |
| 介電常數 | IEC 60250 | ||
| 1 MHz | 2.03 | ASTM D150 | |
| 1.00 GHz | 2.03 | ASTM D2520 | |
| 耗散因數 | IEC 60250 | ||
| 1 MHz | 6.0E-4 | ASTM D150 | |
| 1.00 GHz | 4.0E-4 | ASTM D2520 | |
| 可燃性 | 額定值 | 單位制 | 測試方法 |
| UL 阻燃等級1 | V-0 | UL 94 | |
| 極限氧指數 | > 95 | % | ASTM D2863,ISO 4589-2 |
| 補充信息 | 額定值 | 單位制 | 測試方法 |
| Critical Shear Rate(372℃) | 200 | sec^-1 | 內部方法 |
| MIT Folding Endurance2(200.0 µm) | 7.0E+3 | Cycles | ASTM D2176 |
| 備注 1These results are based on laboratory tests under controlled conditions and do not reflect performance under actual fire conditions,current rating is a typical theoretical value. 28 mil film |
|||
鐵氟龍™ FEP 聚全氟乙丙烯
連續(xù)最高使用溫度：200℃
極限氧指數（LOI）：95%
﹡Teflon™FEP為四氟乙烯與六氟丙烯的共聚合產物，是一種可以熔融擠出成型的樹脂，因其優(yōu)越的加工性，使得Teflon™的用途增加，連續(xù)最高使用溫度為200°C。
﹡成型法與PFA相同，使用熔融擠出成型、傳遞成型、模壓成型等方法。
﹡Teflon™FEP為四氟乙烯與六氟丙烯的共聚合產物，是一種可以熔融擠出成型的樹脂，連續(xù)最高使用溫度為200°C。
﹡成型法與PFA相同，使用熔融擠出成型、傳遞成型、模壓成型等方法。
﹡與PTFE、PFA具有相似的耐化學藥品性、電氣特性。主要使用于電線絕緣/護套或管材擠出。Teflon™FEP為半透明顆粒料。
﹡FEP加工時，所有與其熔體接觸的部件都必須采用耐腐蝕性材料如鎳基合金等。