VALOX™ ENH8560
Generic Name: 聚對(duì)苯二甲酸丁二酯 + PET (PBT+PET) - 提供方: SABIC
VALOX ENH8560 is a 30% glass reinforced, non-chlorinated/brominated flame retardant Polybutylene Terephthalate/Polyethylene Terephthalate (PBT/PET) injection moldable grade with excellent chemical resistance. It has a UL94V0@1.5mm and 5VA@2.0mm flame rating. This is a good candidate for a variety of applications needing a sustainable FR PBT/PET solution.
黃卡號(hào)碼：E45329-100705592
增強(qiáng)材料：玻璃纖維30%增強(qiáng)
材料特性：耐化學(xué)品良好、無溴阻燃、Chlorine Free
材料用途：電氣/電子應(yīng)用領(lǐng)域、電氣元件、電線電纜應(yīng)用
外觀形式：粒子注射成型
供貨地區(qū)：歐洲
物料性能：
| 物理性能 | 額定值 | 單位制 | 測試方法 |
| 密度/比重 | 1.58 | g/cm³ | ASTM D792,ISO 1183 |
| 熔流率（熔體流動(dòng)速率） | |||
| 250℃/5.0 kg | 11 | g/10 min | ASTM D1238,ISO 1133 |
| 265℃/2.16 kg | 5.0 | g/10 min | ASTM D1238 |
| 溶化體積流率（MVR） | |||
| 250℃/5.0 kg | 10 | cm³/10min | ASTM D1238 |
| 265℃/5.0 kg | 25 | cm³/10min | ISO 1133 |
| 收縮率 - 流動(dòng)1 | 0.30 到 0.40 | % | 內(nèi)部方法 |
| 吸水率 | |||
| 24 hr,23℃,50% RH | 0.070 | % | ASTM D570 |
| 24 hr,23℃ | 0.40 | % | ASTM D570 |
| 飽和,23℃ | 0.30 | % | ISO 62 |
| 平衡,23℃,50% RH | 0.050 | % | ISO 62 |
| 機(jī)械性能 | 額定值 | 單位制 | 測試方法 |
| 拉伸模量 | |||
| --2 | 12000 | MPa | ASTM D638 |
| -- | 12000 | MPa | ISO 527-1/1 |
| 抗張強(qiáng)度 | |||
| 屈服3 | 103 | MPa | ASTM D638 |
| 屈服 | 105 | MPa | ISO 527-2/5 |
| 斷裂3 | 103 | MPa | ASTM D638 |
| 斷裂 | 105 | MPa | ISO 527-2/5 |
| 伸長率 | |||
| 屈服3 | 1.0 | % | ASTM D638 |
| 屈服 | 1.0 | % | ISO 527-2/5 |
| 斷裂3 | 2.0 | % | ASTM D638 |
| 斷裂 | 2.0 | % | ISO 527-2/5 |
| 彎曲模量 | |||
| 50.0 mm 跨距4 | 10000 | MPa | ASTM D790 |
| --5 | 10000 | MPa | ISO 178 |
| 彎曲應(yīng)力 | |||
| --5,6 | 165 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距4 | 145 | MPa | ASTM D790 |
| 斷裂,50.0 mm 跨距4 | 145 | MPa | ASTM D790 |
| 彎曲應(yīng)變 - at Break7 | 2.0 | % | ISO 178 |
| 沖擊性能 | 額定值 | 單位制 | 測試方法 |
| 簡支梁缺口沖擊強(qiáng)度 | |||
| -30℃ | 7.0 | kJ/m² | ISO 179/2C |
| 23℃8 | 5.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 7.0 | kJ/m² | ISO 179/2C |
| 簡支梁無缺口沖擊強(qiáng)度 | ISO 179/2U | ||
| -30℃ | 30 | kJ/m² | |
| 23℃ | 30 | kJ/m² | |
| 懸壁梁缺口沖擊強(qiáng)度 | |||
| -30℃ | 60 | J/m | ASTM D256 |
| 0℃ | 60 | J/m | ASTM D256 |
| 23℃ | 60 | J/m | ASTM D256 |
| -30℃9 | 7.0 | kJ/m² | ISO 180/1A |
| 0℃12 | 7.0 | kJ/m² | ISO 180/1A |
| 23℃9 | 7.0 | kJ/m² | ISO 180/1A |
| 無缺口懸臂梁沖擊 | |||
| -30℃ | 400 | J/m | ASTM D4812 |
| 23℃ | 450 | J/m | ASTM D4812 |
| -30℃9 | 27 | kJ/m² | ISO 180/1U |
| 23℃9 | 30 | kJ/m² | ISO 180/1U |
| 硬度 | 額定值 | 單位制 | 測試方法 |
| 洛氏硬度(R 計(jì)秤) | 118 | ISO 2039-2 | |
| 球壓硬度(H 358/30) | 166 | MPa | ISO 2039-1 |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
| 載荷下熱變形溫度 | |||
| 0.45 MPa,未退火,3.20 mm | 210 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,4.00 mm,64.0mm 跨距9 | 215 | ℃ | ISO 75-2/Bf |
| 1.8 MPa,未退火,3.20 mm | 196 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,64.0mm 跨距9 | 180 | ℃ | ISO 75-2/Af |
| 維卡軟化溫度 | |||
| -- | 220 | ℃ | ASTM D152510 |
| -- | 196 | ℃ | ASTM D152511 |
| -- | 201 | ℃ | ISO 306/B120 |
| -- | 203 | ℃ | ISO 306/B50 |
| -- | 215 | ℃ | ISO 306/A50 |
| Ball Pressure Test(123到127℃) | 通過 | IEC 60695-10-2 | |
| 線形熱膨脹系數(shù) | |||
| 流動(dòng):-40 到 95℃ | 2.1E-5 | cm/cm/℃ | ASTM E831 |
| 流動(dòng):-40 到 40℃ | 1.9E-5 | cm/cm/℃ | ISO 11359-2 |
| 流動(dòng):23 到 150℃ | 2.1E-5 | cm/cm/℃ | ISO 11359-2 |
| 垂直:-40 到 95℃ | 5.6E-5 | cm/cm/℃ | ASTM E831 |
| 垂直:-40 到 40℃ | 5.6E-5 | cm/cm/℃ | ISO 11359-2 |
| 垂直:23 到 150℃ | 1.4E-4 | cm/cm/℃ | ISO 11359-2 |
| RTI Elec | 75.0 | ℃ | UL 746B |
| RTI Imp | 75.0 | ℃ | UL 746B |
| RTI | 75.0 | ℃ | UL 746B |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
| 表面電阻率 | > 1.0E+15 | ohms | IEC 60093 |
| 體積電阻率 | 1.0E+15 | ohms·cm | ASTM D257,IEC 60093 |
| 介電強(qiáng)度 | |||
| 0.800 mm,in Oil | 35 | kV/mm | ASTM D149 |
| 1.60 mm,in Oil | 25 | kV/mm | ASTM D149 |
| 3.20 mm,in Oil | 8.0 | kV/mm | ASTM D149 |
| 0.800 mm,在油中 | 35 | kV/mm | IEC 60243-1 |
| 1.60 mm,在油中 | 25 | kV/mm | IEC 60243-1 |
| 3.20 mm,在油中 | 8.0 | kV/mm | IEC 60243-1 |
| 介電常數(shù)(1 MHz) | 3.60 | ASTM D150,IEC 60250 | |
| 耗散因數(shù)(1 MHz) | 0.012 | ASTM D150,IEC 60250 | |
| 相比耐漏電起痕指數(shù)(CTI) | PLC 2 | UL 746A | |
| 漏電起痕指數(shù)12 | 425 | V | IEC 60112 |
| 高電弧燃燒指數(shù)(HAI)(> 0.8 mm) | PLC 0 | UL 746A | |
| 熱絲引燃 (HWI)(> 0.8 mm) | PLC 0 | UL 746A | |
| 可燃性 | 額定值 | 單位制 | 測試方法 |
| UL 阻燃等級(jí) | UL 94 | ||
| > 1.5 mm | V-0 | ||
| > 2.0 mm | 5VA | ||
| 灼熱絲易燃指數(shù) | IEC 60695-2-12 | ||
| 0.8 mm | 960 | ℃ | |
| 1.5 mm | 960 | ℃ | |
| 2.0 mm | 960 | ℃ | |
| 3.0 mm | 960 | ℃ | |
| 熱燈絲點(diǎn)火溫度 | IEC 60695-2-13 | ||
| 0.8 mm | 750 | ℃ | |
| 1.0 mm | 750 | ℃ | |
| 1.5 mm | 750 | ℃ | |
| 2.0 mm | 775 | ℃ | |
| 3.0 mm | 825 | ℃ | |
| 極限氧指數(shù) | 31 | % | ASTM D2863,ISO 4589-2 |
| 充模分析 | 額定值 | 單位制 | 測試方法 |
| 熔體粘度(260℃,1500 sec^-1) | 155 | Pa·s | ISO 11443 |
| 補(bǔ)充信息 | 額定值 | 單位制 | 測試方法 |
| 填充物 | 30 | % | ASTM D229 |
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 110 到 120 | ℃ | |
| 干燥時(shí)間 | 4.0 到 6.0 | hr | |
| 建議的最大水分含量 | 0.020 | % | |
| 料斗溫度 | 40 到 60 | ℃ | |
| 料筒后部溫度 | 240 到 260 | ℃ | |
| 料筒中部溫度 | 255 到 280 | ℃ | |
| 料筒前部溫度 | 260 到 280 | ℃ | |
| 射嘴溫度 | 265 到 275 | ℃ | |
| 加工（熔體）溫度 | 260 到 285 | ℃ | |
| 模具溫度 | 60 到 110 | ℃ | |
| 備注 1Tensile Bar 25.0 mm/min 3類型 1,5.0 mm/min 41.3 mm/min 52.0 mm/min 6at Break 72 mm/min 880*10*4 sp=62mm 980*10*4 mm 10速率 A (50°C/h),壓 力1 (10N) 11速率 A (50°C/h),載荷2 (50N) 12Value shown here is based on internal measurement. |
|||
聚對(duì)苯二甲酸丁二醇酯，英文名polybutylene terephthalate（簡稱PBT），屬于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)與對(duì)苯二甲酸(PTA)或者對(duì)苯二甲酸酯(DMT)聚縮合而成，分子式為(C8H8·C4H6·C3H3N)x，并經(jīng)由混煉程序制成的乳白色半透明到不透明、結(jié)晶型熱塑性聚酯樹脂。與PET一起統(tǒng)稱為熱塑性聚酯，或飽和聚酯。PBT是最堅(jiān)韌的工程熱塑材料之一，它是半結(jié)晶材料，有非常好的化學(xué)穩(wěn)定性、機(jī)械強(qiáng)度、電絕緣特性和熱穩(wěn)定性。