VALOX™ 420SE0
Generic Name: 聚丁烯對苯二甲酸酯(PBT) - 提供方: SABIC
VALOX 420SE0 is a 30% glass filled, flame retardant Polybutylene Terephthalate (PBT) injection moldable grade with excellent chemical resistance. It has a UL94V0@0.71mm and 5VA@2.0mm flame rating. This is a good candidate for a variety of applications in the electrical industry including commutators, cooling fan components, connectors, bobbins, and switches.
黃卡號碼：E45587-101092091、E207780-101092084、E207780-101513785、E45587-101513788
材料用途：Material Handling、Recreational Vehicle Applications、Water Management、電氣/電子應(yīng)用領(lǐng)域、電氣元件、電器用具、電子顯示器、非特定食品應(yīng)用、工業(yè)應(yīng)用、航空航天應(yīng)用、建筑應(yīng)用領(lǐng)域、汽車的發(fā)動機罩下的零件、汽車內(nèi)部零件、汽車外部零件、汽車照明、體育用品、醫(yī)療/護理用品、照明應(yīng)用
供貨地區(qū)：亞太地區(qū)
| 物理性能 | 額定值 | 單位制 | 測試方法 |
| 密度/比重 | 1.63 | g/cm³ | ASTM D792,ISO 1183 |
| 特定體積 | 0.610 | cm³/g | ASTM D792 |
| 熔流率（熔體流動速率）(250℃/5.0 kg) | 42 | g/10 min | ASTM D1238 |
| 熔融體積流量（MVR）(250℃/5.0 kg) | 29 | cm³/10min | ISO 1133 |
| 收縮率 | 內(nèi)部方法 | ||
| 垂直1 | 0.40 到 0.80 | % | |
| 流動1 | 0.10 到 0.50 | % | |
| 垂直:3.20 mm | 0.50 到 1.0 | % | |
| 流動:3.20 mm | 0.50 到 0.70 | % | |
| 吸水率 | ISO 62 | ||
| 飽和,23℃ | 0.090 | % | |
| 平衡,23℃,50% RH | 0.070 | % | |
| 室外適用性 | f2 | UL 746C | |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
| 拉伸模量 | |||
| --2 | 12000 | MPa | ASTM D638 |
| -- | 10000 | MPa | ISO 527-1/1 |
| 抗張強度 | |||
| 屈服3 | 120 | MPa | ASTM D638 |
| 屈服 | 120 | MPa | ISO 527-2/5 |
| 斷裂3 | 120 | MPa | ASTM D638 |
| 斷裂 | 120 | MPa | ISO 527-2/5 |
| 伸長率 | |||
| 屈服3 | 2.0 | % | ASTM D638 |
| 屈服 | 1.9 | % | ISO 527-2/5 |
| 斷裂3 | 2.0 | % | ASTM D638 |
| 斷裂 | 1.9 | % | ISO 527-2/5 |
| 彎曲模量 | |||
| 50.0 mm 跨距4 | 9800 | MPa | ASTM D790 |
| --5 | 9500 | MPa | ISO 178 |
| 彎曲應(yīng)力 | |||
| -- | 180 | MPa | ISO 178 |
| 斷裂,50.0 mm 跨距4 | 186 | MPa | ASTM D790 |
| 泰伯耐磨性(1000 Cycles,1000 g,CS-17 轉(zhuǎn)輪) | 22.0 | mg | 內(nèi)部方法 |
| 沖擊性能 | 額定值 | 單位制 | 測試方法 |
| 簡支梁缺口沖擊強度6 | ISO 179/1eA | ||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 7.0 | kJ/m² | |
| 簡支梁無缺口沖擊強度6 | ISO 179/1eU | ||
| -30℃ | 50 | kJ/m² | |
| 23℃ | 50 | kJ/m² | |
| 懸壁梁缺口沖擊強度 | |||
| -30℃ | 57 | J/m | ASTM D256 |
| 23℃ | 60 | J/m | ASTM D256 |
| -30℃7 | 6.0 | kJ/m² | ISO 180/1A |
| 23℃7 | 7.0 | kJ/m² | ISO 180/1A |
| 無缺口懸臂梁沖擊 | |||
| 23℃ | 620 | J/m | ASTM D4812 |
| -30℃7 | 45 | kJ/m² | ISO 180/1U |
| 23℃7 | 45 | kJ/m² | ISO 180/1U |
| 裝有測量儀表的落鏢沖擊(23℃,Total Energy) | 5.00 | J | ASTM D3763 |
| 硬度 | 額定值 | 單位制 | 測試方法 |
| 洛氏硬度 | |||
| R 級 | 119 | ASTM D785 | |
| R 計秤 | 119 | ISO 2039-2 | |
| 球壓硬度(H 358/30) | 118 | MPa | ISO 2039-1 |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
| 載荷下熱變形溫度 | |||
| 0.45 MPa,未退火,3.20 mm | 212 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,4.00 mm,100 mm 跨距8 | 220 | ℃ | ISO 75-2/Be |
| 1.8 MPa,未退火,3.20 mm | 200 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,100 mm 跨距8 | 195 | ℃ | ISO 75-2/Ae |
| 1.8 MPa,未退火,4.00 mm,64.0 mm 跨距7 | 200 | ℃ | ISO 75-2/Af |
| 維卡軟化溫度 | |||
| -- | 200 | ℃ | ASTM D15259,ISO 306/B120,ISO 306/B50 |
| -- | 220 | ℃ | ISO 306/A50 |
| Ball Pressure Test(123 到 127℃) | 通過 | IEC 60695-10-2 | |
| 線形熱膨脹系數(shù) | |||
| 流動:-40 到 40℃ | 2.5E-5 | cm/cm/℃ | ASTM E831,ISO 11359-2 |
| 流動:23 到 80℃ | 2.5E-5 | cm/cm/℃ | ISO 11359-2 |
| 垂直:-40 到 40℃ | 8.9E-5 | cm/cm/℃ | ASTM E831,ISO 11359-2 |
| 垂直:23 到 80℃ | 1.2E-4 | cm/cm/℃ | ISO 11359-2 |
| 導(dǎo)熱系數(shù) | 0.25 | W/m/K | ISO 8302 |
| RTI Elec | 130 | ℃ | UL 746B |
| RTI Imp | 130 | ℃ | UL 746B |
| RTI | 140 | ℃ | UL 746B |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
| 表面電阻率 | > 1.0E+15 | ohms | IEC 60093 |
| 體積電阻率 | > 1.0E+15 | ohms·cm | ASTM D257,IEC 60093 |
| 介電強度 | |||
| 1.60 mm,in Oil | 24 | kV/mm | ASTM D149 |
| 3.20 mm,in Air | 19 | kV/mm | ASTM D149 |
| 0.800 mm,在油中 | 23 | kV/mm | IEC 60243-1 |
| 1.60 mm,在油中 | 22 | kV/mm | IEC 60243-1 |
| 3.20 mm,在油中 | 16 | kV/mm | IEC 60243-1 |
| 介電常數(shù) | |||
| 100 Hz | 3.80 | ASTM D150,IEC 60250 | |
| 1 MHz | 3.70 | ASTM D150 | |
| 50 Hz | 3.30 | IEC 60250 | |
| 60 Hz | 3.30 | IEC 60250 | |
| 1 MHz | 3.30 | IEC 60250 | |
| 耗散因數(shù) | |||
| 100 Hz | 2.0E-3 | ASTM D150,IEC 60250 | |
| 1 MHz | 0.020 | ASTM D150 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 | |
| 耐電弧性10 | PLC 6 | ASTM D495 | |
| 相比耐漏電起痕指數(shù)(CTI) | PLC 3 | UL 746A | |
| 漏電起痕指數(shù) | IEC 60112 | ||
| -- | 175 | V | |
| 解決方案 B | 125 | V | |
| 高電弧燃燒指數(shù)(HAI)11 | PLC 0 | UL 746A | |
| 高壓電弧抗點燃指數(shù) (HVAR) (PLC) | PLC 4 | UL 746A | |
| 熱絲引燃 (HWI) | PLC 2 | UL 746A | |
| 可燃性 | 額定值 | 單位制 | 測試方法 |
| UL 阻燃等級 | UL 94 | ||
| 0.40 mm | V-2 | ||
| 0.71 mm | V-0 | ||
| 2.0 mm | 5VA | ||
| 灼熱絲易燃指數(shù)(1.0 mm) | 960 | ℃ | IEC 60695-2-12 |
| 極限氧指數(shù) | 32 | % | ISO 4589-2 |
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 120 | ℃ | |
| 干燥時間 | 3.0 到 4.0 | hr | |
| 建議的最大水分含量 | 0.020 | % | |
| 建議注射量 | 40 到 80 | % | |
| 料筒后部溫度 | 245 到 265 | ℃ | |
| 料筒中部溫度 | 250 到 270 | ℃ | |
| 料筒前部溫度 | 255 到 275 | ℃ | |
| 射嘴溫度 | 250 到 270 | ℃ | |
| 加工（熔體）溫度 | 255 到 275 | ℃ | |
| 模具溫度 | 65 到 90 | ℃ | |
| 背壓 | 0.300 到 0.700 | MPa | |
| 螺桿轉(zhuǎn)速 | 50 到 80 | rpm | |
| 排氣孔深度 | 0.025 到 0.038 | mm | |
| 注射說明 Drying Time (Cumulative): 12 hr 備注 1Tensile Bar 25.0 mm/min 3類型 1,5.0 mm/min 41.3 mm/min 52.0 mm/min 680*10*4 sp=62mm 780*10*4 mm 8120*10*4 mm 9速率 A (50℃/h),載荷2 (50N) 10鎢電極 11Surface |
|||